Prediction of sulfate attack products in Portland-limestone cements: the effect of cation type and concentration
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378297%3A_____%2F21%3A00546427" target="_blank" >RIV/68378297:_____/21:00546427 - isvavai.cz</a>
Výsledek na webu
<a href="https://doi.org/10.4028/www.scientific.net/SSP.325.28" target="_blank" >https://doi.org/10.4028/www.scientific.net/SSP.325.28</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.325.28" target="_blank" >10.4028/www.scientific.net/SSP.325.28</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Prediction of sulfate attack products in Portland-limestone cements: the effect of cation type and concentration
Popis výsledku v původním jazyce
Portland-limestone cement materials are susceptible to sulfate attack at low temperature and high humidity, because such conditions facilitate the formation of thaumasite, detriment to the structural integrity of calcium silicate hydrates (C─S─H). In this work, the effect of the cation associated with sulfates, concentration of sulfate solution, and limestone content in cement, were thermodynamically simulated. MgSO4 solution is of higher risk, degrading extensively the structural integrity of C─S─H. Although this phase is partially preserved under the effect of Na2SO4 and K2SO4 solutions, extensive expansion and thaumasite formation occur. The sulfate content of the corrosive solution and the limestone content in cement are the factors mostly intensifying the attack caused by MgSO4 and Na2SO4/K2SO4 solutions, respectively.
Název v anglickém jazyce
Prediction of sulfate attack products in Portland-limestone cements: the effect of cation type and concentration
Popis výsledku anglicky
Portland-limestone cement materials are susceptible to sulfate attack at low temperature and high humidity, because such conditions facilitate the formation of thaumasite, detriment to the structural integrity of calcium silicate hydrates (C─S─H). In this work, the effect of the cation associated with sulfates, concentration of sulfate solution, and limestone content in cement, were thermodynamically simulated. MgSO4 solution is of higher risk, degrading extensively the structural integrity of C─S─H. Although this phase is partially preserved under the effect of Na2SO4 and K2SO4 solutions, extensive expansion and thaumasite formation occur. The sulfate content of the corrosive solution and the limestone content in cement are the factors mostly intensifying the attack caused by MgSO4 and Na2SO4/K2SO4 solutions, respectively.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/GJ18-26056Y" target="_blank" >GJ18-26056Y: Experimentální kvantifikace a modelování degradace směsných cementových past s příměsí vápence vlivem síranové koroze za vzniku thaumasitu</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2021
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Solid State Phenomena
ISBN
978-3-0357-1870-6
ISSN
1662-9779
e-ISSN
—
Počet stran výsledku
6
Strana od-do
28-33
Název nakladatele
Trans Tech Publications
Místo vydání
Baech
Místo konání akce
Brno
Datum konání akce
3. 12. 2020
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—