Fatigue of Reinforced Concrete Bridges with Influence of Deterioration of Concrete

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F08%3A00157310" target="_blank" >RIV/68407700:21110/08:00157310 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue of Reinforced Concrete Bridges with Influence of Deterioration of Concrete

Popis výsledku v původním jazyce

Fatigue is a process of permanent progressive changes in the structure of a material exposed to cyclic loading. High stress ranges in these structures can cause crack propagation, consequently reduce stiffness and can lead to fatigue failure. Also, exposing the material to aggressive environment can result in material deterioration, which accelerates the decrease of fatigue performance of the construction. The prediction of deflections, and thus serviceability, of concrete bridges subjected to cyclic loading can be calculated by using a fatigue damage function. This function expresses reduced structural stiffness by decreasing of the modulus of elasticity depending on the number of load cycles. In this paper, an application of this function is shown inan illustrative example of a small concrete bridge.

Název v anglickém jazyce

Fatigue of Reinforced Concrete Bridges with Influence of Deterioration of Concrete

Popis výsledku anglicky

Fatigue is a process of permanent progressive changes in the structure of a material exposed to cyclic loading. High stress ranges in these structures can cause crack propagation, consequently reduce stiffness and can lead to fatigue failure. Also, exposing the material to aggressive environment can result in material deterioration, which accelerates the decrease of fatigue performance of the construction. The prediction of deflections, and thus serviceability, of concrete bridges subjected to cyclic loading can be calculated by using a fatigue damage function. This function expresses reduced structural stiffness by decreasing of the modulus of elasticity depending on the number of load cycles. In this paper, an application of this function is shown inan illustrative example of a small concrete bridge.

Druh

D - Stať ve sborníku

CEP obor

JN - Stavebnictví

OECD FORD obor

—

Projekt

—

Návaznosti

V - Vyzkumna aktivita podporovana z jinych verejnych zdroju

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Microstructure Related Durability of Cementitious Composites

ISBN

978-2-35158-065-3

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

—

Název nakladatele

Rilem Publications s.a.r.l.

Místo vydání

Bagneux

Místo konání akce

Nanjing

Datum konání akce

13. 10. 2008

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000262079600088