Relationship between mechanical strength and Young's modulus in traditional ceramics

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F11%3A00182812" target="_blank" >RIV/68407700:21110/11:00182812 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26110/11:PU97457

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Relationship between mechanical strength and Young's modulus in traditional ceramics

Popis výsledku v původním jazyce

A verification of theoretical linearity between mechanical strength and Young's modulus was performed with quartz porcelain samples both green and fired. The experiments were carried out at the room temperature and at elevated temperatures up to 1000 °C.The results obtained for green samples showed relatively scattered values around the linear function. A regression coefficient of the linear fitting (R = 0.803) is not sufficient for a clear linearity . The relationship is clearly linear for a fired sample and was confirmed in the temperature interval 20-1000 °C. For this case, the regression coefficient of the linear fitting is 0.976.

Název v anglickém jazyce

Relationship between mechanical strength and Young's modulus in traditional ceramics

Popis výsledku anglicky

A verification of theoretical linearity between mechanical strength and Young's modulus was performed with quartz porcelain samples both green and fired. The experiments were carried out at the room temperature and at elevated temperatures up to 1000 °C.The results obtained for green samples showed relatively scattered values around the linear function. A regression coefficient of the linear fitting (R = 0.803) is not sufficient for a clear linearity . The relationship is clearly linear for a fired sample and was confirmed in the temperature interval 20-1000 °C. For this case, the regression coefficient of the linear fitting is 0.976.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/MEB0810008" target="_blank" >MEB0810008: Studium procesu výpalu keramického střepu na bázi popílkojílové surovinové směsi</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials and Technology

ISSN

1580-2949

e-ISSN

—

Svazek periodika

43

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

SI - Slovinská republika

Počet stran výsledku

4

Strana od-do

375-378

Kód UT WoS článku

000294086000014

EID výsledku v databázi Scopus

—