Prediction of Carbonation and Chloride Ingress in Cracked Concrete Structures

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F13%3A00209888" target="_blank" >RIV/68407700:21110/13:00209888 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Prediction of Carbonation and Chloride Ingress in Cracked Concrete Structures

Popis výsledku v původním jazyce

Carbonation and chloride ingress are the most relevant damaging mechanisms for steel corrosion in reinforced concrete structures. Massive utilization of supplementary cementitious materials in cement binders implies recalibration of existing models for these phenomena. The carbonation model formulated by Papadakis and the model for chloride ingress from Kwon are extended for crack effects, which accelerates both damaging mechanisms. Both models were reformulated in an incremental form, allowing a gradual crack growth. It was found that the crack width 0.3 mm decreases the induction time approximately five times when compared to uncracked concrete. Validation on in situ samples shows good predictions for chloride profiles.

Název v anglickém jazyce

Prediction of Carbonation and Chloride Ingress in Cracked Concrete Structures

Popis výsledku anglicky

Carbonation and chloride ingress are the most relevant damaging mechanisms for steel corrosion in reinforced concrete structures. Massive utilization of supplementary cementitious materials in cement binders implies recalibration of existing models for these phenomena. The carbonation model formulated by Papadakis and the model for chloride ingress from Kwon are extended for crack effects, which accelerates both damaging mechanisms. Both models were reformulated in an incremental form, allowing a gradual crack growth. It was found that the crack width 0.3 mm decreases the induction time approximately five times when compared to uncracked concrete. Validation on in situ samples shows good predictions for chloride profiles.

Druh

D - Stať ve sborníku

CEP obor

JN - Stavebnictví

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of the Fourteenth International Conference on Civil, Structural and Environmental Engineering Computing

ISBN

978-1-905088-57-7

ISSN

1759-3433

e-ISSN

—

Počet stran výsledku

12

Strana od-do

1-12

Název nakladatele

Civil-Comp Press Ltd

Místo vydání

Stirling

Místo konání akce

Cagliari

Datum konání akce

3. 9. 2013

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—