DETERMINATION OF STEEL CORROSION RATE
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F16%3A00302098" target="_blank" >RIV/68407700:21110/16:00302098 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
DETERMINATION OF STEEL CORROSION RATE
Popis výsledku v původním jazyce
Carbonation and chloride ingress are considered as the most serious damaging mechanisms for steel corrosion in reinforced concrete. The service life is divided into two main phases. The initial phase and propagation phase. The initial phase was explored recently and results show high influence of cracks on accelerating of carbonation and chloride ingress in concrete structures. Our model focuses on the propagation period and predicts x corr presents a loss of mass for radial corrosion depth, including cracking and spalling of concrete cover. The presented model was implemented in ATENA software. A prestressed box-girder bridge is analyzed in greater detail, showing corrosion of reinforcement and its impact on bridge’s bearing capacity.
Název v anglickém jazyce
DETERMINATION OF STEEL CORROSION RATE
Popis výsledku anglicky
Carbonation and chloride ingress are considered as the most serious damaging mechanisms for steel corrosion in reinforced concrete. The service life is divided into two main phases. The initial phase and propagation phase. The initial phase was explored recently and results show high influence of cracks on accelerating of carbonation and chloride ingress in concrete structures. Our model focuses on the propagation period and predicts x corr presents a loss of mass for radial corrosion depth, including cracking and spalling of concrete cover. The presented model was implemented in ATENA software. A prestressed box-girder bridge is analyzed in greater detail, showing corrosion of reinforcement and its impact on bridge’s bearing capacity.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JM - Inženýrské stavitelství
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/TA04031458" target="_blank" >TA04031458: Software pro predikci a modelování životnosti a bezpečnosti dopravních konstrukcí</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Engineering Mechanics 2016 - Book of full texts
ISBN
978-80-87012-59-8
ISSN
1805-8248
e-ISSN
—
Počet stran výsledku
4
Strana od-do
186-189
Název nakladatele
Institute of Thermomechanics, AS CR, v.v.i.
Místo vydání
Prague
Místo konání akce
Svratka
Datum konání akce
9. 5. 2016
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000379986700031