Preparation and properties of fly ash-based geopolymer foams

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F14%3A00225631" target="_blank" >RIV/68407700:21110/14:00225631 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/60461373:22310/14:43898400

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Preparation and properties of fly ash-based geopolymer foams

Popis výsledku v původním jazyce

An extremely porous geopolymer material ? an incombustible alumino-silicate foam ? can be prepared by incorporating gas-forming agents into mixtures consisting of an alkaline activating agent (NaOH + sodium water glass) and fly ash. Aluminium powder or materials containing elemental Si (silica fume, FeSi or SiC) may be used as gas-forming agents. Macroscopic pores are given rise thanks to the release of gaseous hydrogen generated during the reaction of aluminium, respectively Si, in a strong alkaline environment. The formation of the foam becomes more intense if aluminium powder is used instead of silica fume. The effect of silica fume can only be observed at concentrations ranging from 5 to 10 percent by weight and at temperatures above 60°C because of a low content of elemental Si in silica fume. The foam formation takes place immediately after the addition of aluminium powder to the mixture but the foam collapsing must be prevented by incorporation of portland cement or lime. The Si

Název v anglickém jazyce

Preparation and properties of fly ash-based geopolymer foams

Popis výsledku anglicky

An extremely porous geopolymer material ? an incombustible alumino-silicate foam ? can be prepared by incorporating gas-forming agents into mixtures consisting of an alkaline activating agent (NaOH + sodium water glass) and fly ash. Aluminium powder or materials containing elemental Si (silica fume, FeSi or SiC) may be used as gas-forming agents. Macroscopic pores are given rise thanks to the release of gaseous hydrogen generated during the reaction of aluminium, respectively Si, in a strong alkaline environment. The formation of the foam becomes more intense if aluminium powder is used instead of silica fume. The effect of silica fume can only be observed at concentrations ranging from 5 to 10 percent by weight and at temperatures above 60°C because of a low content of elemental Si in silica fume. The foam formation takes place immediately after the addition of aluminium powder to the mixture but the foam collapsing must be prevented by incorporation of portland cement or lime. The Si

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JN - Stavebnictví

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP104%2F12%2F0102" target="_blank" >GAP104/12/0102: Alumosilikátové polymerní pěny</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Ceramics - Silikáty

ISSN

0862-5468

e-ISSN

—

Svazek periodika

58

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

10

Strana od-do

188-197

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—