Development of Young?s Modulus of Illitic Clay during Heating up to 1100 °C

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F15%3A00233563" target="_blank" >RIV/68407700:21110/15:00233563 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.5755/j01.ms.21.3.7152" target="_blank" >http://dx.doi.org/10.5755/j01.ms.21.3.7152</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.5755/j01.ms.21.3.7152" target="_blank" >10.5755/j01.ms.21.3.7152</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Development of Young?s Modulus of Illitic Clay during Heating up to 1100 °C

Popis výsledku v původním jazyce

Young?s modulus of green illite from Füzérradvány (Hungary) was measured in-situ in the temperature interval 20 °C ? 1100 °C and auxiliary analyses DTA, TG and TDA, XRD and EGA, were also performed. It was found that a removal of the physically bound water (20 °C ? 250 °C) sets illite crystals closer, which leads to a significant increase of Young?s modulus from its initial value of 7 GPa to the maximum 12 GPa at 300 °C. Young?s modulus slightly decreases in the temperature interval of dehydroxylation of illite (300 °C ? 800 °C), and which then reaches up to 45 GPa at 1100 °C, increasing exponentially as a consequence of the sintering above 800 °C.

Název v anglickém jazyce

Development of Young?s Modulus of Illitic Clay during Heating up to 1100 °C

Popis výsledku anglicky

Young?s modulus of green illite from Füzérradvány (Hungary) was measured in-situ in the temperature interval 20 °C ? 1100 °C and auxiliary analyses DTA, TG and TDA, XRD and EGA, were also performed. It was found that a removal of the physically bound water (20 °C ? 250 °C) sets illite crystals closer, which leads to a significant increase of Young?s modulus from its initial value of 7 GPa to the maximum 12 GPa at 300 °C. Young?s modulus slightly decreases in the temperature interval of dehydroxylation of illite (300 °C ? 800 °C), and which then reaches up to 45 GPa at 1100 °C, increasing exponentially as a consequence of the sintering above 800 °C.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GBP105%2F12%2FG059" target="_blank" >GBP105/12/G059: Kumulativní časově závislé procesy ve stavebních materiálech a konstrukcích</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Science

ISSN

1392-1320

e-ISSN

—

Svazek periodika

21

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

LT - Litevská republika

Počet stran výsledku

6

Strana od-do

429-434

Kód UT WoS článku

000360971300022

EID výsledku v databázi Scopus

2-s2.0-84940848689