The Effect of Micronized Waste Marble Powder as Partial Replacement for Cement on Resulting Mechanical Properties of Cement Pastes
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F16%3A00305957" target="_blank" >RIV/68407700:21110/16:00305957 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/AMR.1144.54" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/AMR.1144.54</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/AMR.1144.54" target="_blank" >10.4028/www.scientific.net/AMR.1144.54</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The Effect of Micronized Waste Marble Powder as Partial Replacement for Cement on Resulting Mechanical Properties of Cement Pastes
Popis výsledku v původním jazyce
This article was focused on the influence of the micronized waste marble powder on mechanical properties of cement pastes. Resulting blended cement was composed of Portland cement CEM I 42.5 R and micronized marble powder with different percentage amounts (0 wt. %, 5 wt. %, 10 wt. % and 15 wt. %). Testing was carried at prismatic samples of dimension 40 x 40 x 160 mm. The investigated mechanical properties were dynamic modulus of elasticity, dynamic shear modulus, flexural strength and compressive strength for the 28 days old samples. The results obtained from these materials were compared with reference material.
Název v anglickém jazyce
The Effect of Micronized Waste Marble Powder as Partial Replacement for Cement on Resulting Mechanical Properties of Cement Pastes
Popis výsledku anglicky
This article was focused on the influence of the micronized waste marble powder on mechanical properties of cement pastes. Resulting blended cement was composed of Portland cement CEM I 42.5 R and micronized marble powder with different percentage amounts (0 wt. %, 5 wt. %, 10 wt. % and 15 wt. %). Testing was carried at prismatic samples of dimension 40 x 40 x 160 mm. The investigated mechanical properties were dynamic modulus of elasticity, dynamic shear modulus, flexural strength and compressive strength for the 28 days old samples. The results obtained from these materials were compared with reference material.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JN - Stavebnictví
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Modern Methods of Experimental and Computational Investigations in Area of Construction II
ISBN
978-3-0357-1092-2
ISSN
1022-6680
e-ISSN
—
Počet stran výsledku
5
Strana od-do
54-58
Název nakladatele
Trans Tech Publications Inc.
Místo vydání
Pfaffikon
Místo konání akce
Praha
Datum konání akce
22. 9. 2016
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—