Utilization of the waste from the marble industry for application in transport infrastructure: mechanical properties of cement pastes

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F17%3A00313635" target="_blank" >RIV/68407700:21110/17:00313635 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21720/17:00313635

Výsledek na webu

<a href="http://iopscience.iop.org/article/10.1088/1757-899X/236/1/012092" target="_blank" >http://iopscience.iop.org/article/10.1088/1757-899X/236/1/012092</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1088/1757-899X/236/1/012092" target="_blank" >10.1088/1757-899X/236/1/012092</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Utilization of the waste from the marble industry for application in transport infrastructure: mechanical properties of cement pastes

Popis výsledku v původním jazyce

This article is focused on the mechanical testing of cement-based samples containing a micronized waste marble powder used as replacement of standard binders. Tested materials consisted of cement CEM I 42.5 R (Radotín, Czech Republic) and three different amount of the marbles (25, 50 and 70 wt. %). Standard bending and compressive tests of the prismatic samples having dimensions equal to 40 x 40 x 160 mm were done in order to reveal an influence of marbles amount on flexural and compressive strength, respectively. Moreover, the dynamic modulus of elasticity and dynamic shear modulus were examined and each other compared after 7 and 28 days of mixture curing.

Název v anglickém jazyce

Utilization of the waste from the marble industry for application in transport infrastructure: mechanical properties of cement pastes

Popis výsledku anglicky

This article is focused on the mechanical testing of cement-based samples containing a micronized waste marble powder used as replacement of standard binders. Tested materials consisted of cement CEM I 42.5 R (Radotín, Czech Republic) and three different amount of the marbles (25, 50 and 70 wt. %). Standard bending and compressive tests of the prismatic samples having dimensions equal to 40 x 40 x 160 mm were done in order to reveal an influence of marbles amount on flexural and compressive strength, respectively. Moreover, the dynamic modulus of elasticity and dynamic shear modulus were examined and each other compared after 7 and 28 days of mixture curing.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20101 - Civil engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Building up Efficient and Sustainable Transport Infrastructure 2017 (BESTInfra2017)

ISBN

—

ISSN

1757-8981

e-ISSN

1757-899X

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

IOP Publishing Ltd

Místo vydání

Bristol

Místo konání akce

Praha

Datum konání akce

20. 9. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000417428700092