Determination of fracture toughness of human enamel by nanoindentation based on energy release method

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F17%3A00312970" target="_blank" >RIV/68407700:21110/17:00312970 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Determination of fracture toughness of human enamel by nanoindentation based on energy release method

Popis výsledku v původním jazyce

Enamel is a brittle material. The main property showing its fracture resistance is fracture toughness. The aim of this study is to determine parameters necessary to estimate fracture toughness by the nanoindentation method. The method of fracture toughness evaluation based on dissipation of energy is described. In the first section of study, changes in values of hardness (HIT) and reduced modulus (Er) are observed with regard to crack initiation and growth. The downward trend of HIT was found with the increasing peak load. The next section is focused on the loading rate impact on crack formation. The results supported the assumption that higher rates of loading induce greater crack formation.

Název v anglickém jazyce

Determination of fracture toughness of human enamel by nanoindentation based on energy release method

Popis výsledku anglicky

Enamel is a brittle material. The main property showing its fracture resistance is fracture toughness. The aim of this study is to determine parameters necessary to estimate fracture toughness by the nanoindentation method. The method of fracture toughness evaluation based on dissipation of energy is described. In the first section of study, changes in values of hardness (HIT) and reduced modulus (Er) are observed with regard to crack initiation and growth. The downward trend of HIT was found with the increasing peak load. The next section is focused on the loading rate impact on crack formation. The results supported the assumption that higher rates of loading induce greater crack formation.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

30404 - Biomaterials (as related to medical implants, devices, sensors)

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Experimental Stress Analysis 2017

ISBN

978-80-553-3167-6

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

15-20

Název nakladatele

Technical University of Kosice

Místo vydání

Košice

Místo konání akce

Nový Smokovec

Datum konání akce

30. 5. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—