The effect of compression pressure on activation energy of spinel formation

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F19%3A00338074" target="_blank" >RIV/68407700:21110/19:00338074 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1063/1.5120132" target="_blank" >https://doi.org/10.1063/1.5120132</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1063/1.5120132" target="_blank" >10.1063/1.5120132</a>

Jazyk výsledku

angličtina

Název v původním jazyce

The effect of compression pressure on activation energy of spinel formation

Popis výsledku v původním jazyce

The paper presents the influence of compression pressure on the apparent activation energy of crystallization of Al-Si spinel phase. This is achieved on the samples which are made from the elecroporcelain mixture under the pressures from 70 MPa up to 110 MPa. The apparent activation energy is determined from the series of non-isothermal thermodilatometry experiments using the Kissinger method. The results show that the apparent activation energy decreases with compression pressure. The determined values of apparent activation energy of samples made with pressures of 70 MPa, 80 MPa, 90 MPa, 100 MPa, and 110 MPa are (670 ± 24) kJ mol-1, (568 ± 40) kJ mol-1, (543 ± 12) kJ mol–1, (526 ± 30) kJ mol–1, and (506 ± 16) kJ mol–1, respectively. The decrease of apparent activation energy with compression pressure may be caused by the decreasing distance between the grains in the material.

Název v anglickém jazyce

The effect of compression pressure on activation energy of spinel formation

Popis výsledku anglicky

The paper presents the influence of compression pressure on the apparent activation energy of crystallization of Al-Si spinel phase. This is achieved on the samples which are made from the elecroporcelain mixture under the pressures from 70 MPa up to 110 MPa. The apparent activation energy is determined from the series of non-isothermal thermodilatometry experiments using the Kissinger method. The results show that the apparent activation energy decreases with compression pressure. The determined values of apparent activation energy of samples made with pressures of 70 MPa, 80 MPa, 90 MPa, 100 MPa, and 110 MPa are (670 ± 24) kJ mol-1, (568 ± 40) kJ mol-1, (543 ± 12) kJ mol–1, (526 ± 30) kJ mol–1, and (506 ± 16) kJ mol–1, respectively. The decrease of apparent activation energy with compression pressure may be caused by the decreasing distance between the grains in the material.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20504 - Ceramics

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Central European Symposium on Thermophysics 2019 (CEST)

ISBN

978-0-7354-1876-9

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

AIP Conference Proceedings

Místo vydání

New York

Místo konání akce

Banská Bystrica, Slovakia

Datum konání akce

16. 10. 2019

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—