Influence of plasma treatment duration on the shear strength of transparent epoxy-bonded glass joints at elevated temperatures: a study using Diffuse Coplanar Surface Barrier Discharge

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F25%3A00386235" target="_blank" >RIV/68407700:21110/25:00386235 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1080/00218464.2025.2572990" target="_blank" >https://doi.org/10.1080/00218464.2025.2572990</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1080/00218464.2025.2572990" target="_blank" >10.1080/00218464.2025.2572990</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of plasma treatment duration on the shear strength of transparent epoxy-bonded glass joints at elevated temperatures: a study using Diffuse Coplanar Surface Barrier Discharge

Popis výsledku v původním jazyce

Plasma treatment is increasingly used to enhance surface proper­ ties in adhesion dependent applications. However, its effects on epoxy-bonded glass under elevated temperatures remain unex­plored. Hence, this research investigates the impact of Diffuse Coplanar Surface Barrier Discharge (DCSBD) plasma treatment duration on the shear strength of epoxy-bonded low-iron glass. Experiments were conducted on glass samples plasma-treated on the tin and air sides for 5, 15, 30, and 60 s, and on untreated references. Specimens were bonded using the epoxy adhesive LOCTITE® EA 9455 and tested under block shear conditions at room temperature (RT), 40°C, and 80°C. The 30 s treatment yielded the highest shear strength at RT, indicating optimal sur­ face activation. Shorter treatments (5–15 s) and prolonged expo­sure (60 s) did not enhance adhesion compared to the reference, indicating that both insufficient and excessive plasma exposure can lead to suboptimal bonding. At elevated temperatures, the shear strength decreased for all conditions, consistent with adhe­sive softening above the glass transition temperature (Tg). These findings highlight the importance of optimising plasma exposure time to balance surface activation with thermal durability. They emphasise additionally the need for further investigation into plasma-induced surface modifications and their stability in bonded assemblies for demanding environments.

Název v anglickém jazyce

Influence of plasma treatment duration on the shear strength of transparent epoxy-bonded glass joints at elevated temperatures: a study using Diffuse Coplanar Surface Barrier Discharge

Popis výsledku anglicky

Plasma treatment is increasingly used to enhance surface proper­ ties in adhesion dependent applications. However, its effects on epoxy-bonded glass under elevated temperatures remain unex­plored. Hence, this research investigates the impact of Diffuse Coplanar Surface Barrier Discharge (DCSBD) plasma treatment duration on the shear strength of epoxy-bonded low-iron glass. Experiments were conducted on glass samples plasma-treated on the tin and air sides for 5, 15, 30, and 60 s, and on untreated references. Specimens were bonded using the epoxy adhesive LOCTITE® EA 9455 and tested under block shear conditions at room temperature (RT), 40°C, and 80°C. The 30 s treatment yielded the highest shear strength at RT, indicating optimal sur­ face activation. Shorter treatments (5–15 s) and prolonged expo­sure (60 s) did not enhance adhesion compared to the reference, indicating that both insufficient and excessive plasma exposure can lead to suboptimal bonding. At elevated temperatures, the shear strength decreased for all conditions, consistent with adhe­sive softening above the glass transition temperature (Tg). These findings highlight the importance of optimising plasma exposure time to balance surface activation with thermal durability. They emphasise additionally the need for further investigation into plasma-induced surface modifications and their stability in bonded assemblies for demanding environments.

Druh

O - Ostatní výsledky

CEP obor

—

OECD FORD obor

20101 - Civil engineering

Projekt

<a href="/cs/project/GA23-06016S" target="_blank" >GA23-06016S: Povrchová úprava skla a její vliv na spolehlivost lepených spojů pro skleněné konstrukce za zvýšené teploty</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2025

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů