Fatigue Threshold and Crack Growth in an Electron Beam Weld Made of Steel and Bronze
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F03%3A00091997" target="_blank" >RIV/68407700:21220/03:00091997 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fatigue Threshold and Crack Growth in an Electron Beam Weld Made of Steel and Bronze
Popis výsledku v původním jazyce
In this research topic some experimental tests with single-edge notched beams were performed to determine the threshold load value for fatigue crack growth and to characterize fatigue crack behaviour of an electron beam weld made of steel and bronze. Subsequently, numerical analyses were done to estimate the threshold value DeltaK(th) and to simulate the fatigue crack growth. The calculated crack path was compared to those determined experimentally. The objective was to find out the necessary fracture properties for an analysis of an electron beam welded worm wheel and to asses the capability of usual fracture analysis software to simulate fatigue crack growth in welds. (C) 2003 Elsevier Ltd. All rights reserved.
Název v anglickém jazyce
Fatigue Threshold and Crack Growth in an Electron Beam Weld Made of Steel and Bronze
Popis výsledku anglicky
In this research topic some experimental tests with single-edge notched beams were performed to determine the threshold load value for fatigue crack growth and to characterize fatigue crack behaviour of an electron beam weld made of steel and bronze. Subsequently, numerical analyses were done to estimate the threshold value DeltaK(th) and to simulate the fatigue crack growth. The calculated crack path was compared to those determined experimentally. The objective was to find out the necessary fracture properties for an analysis of an electron beam welded worm wheel and to asses the capability of usual fracture analysis software to simulate fatigue crack growth in welds. (C) 2003 Elsevier Ltd. All rights reserved.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA101%2F03%2F0620" target="_blank" >GA101/03/0620: Redundantní pohony a měření pro hybridní obráběcí stroj</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2003
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
ENGINEERING FRACTURE MECHANICS
ISSN
0013-7944
e-ISSN
—
Svazek periodika
70
Číslo periodika v rámci svazku
18
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
8
Strana od-do
2617-2624
Kód UT WoS článku
000185162400009
EID výsledku v databázi Scopus
—