Preparation and Characteristics of Al-Cr RST Ribbons

Popis výsledku v původním jazyce

The solubility of Cr in Al is very low, practically zero at an ambient temperature, and it increases only weakly to the maximum of less than mass fraction of 0.5% close to the melting point of pure Al. Cr has on the lowest diffusion coefficient from technically important metals and thus it has also a capability to form very fine and stable precipitates. A supersaturated solid solution must be formed before the alloy can be strengthened by artificial ageing. In the Al-Cr system it is only possible via the rapid solidification procedure because the appropriate solubility of Cr is obtained only in the liquid state and it is retained with practical freezing of the melt. For this two RST procesures are possible: inert gas atomizing and melt spinning.

Název v anglickém jazyce

Preparation and Characteristics of Al-Cr RST Ribbons

Popis výsledku anglicky

The solubility of Cr in Al is very low, practically zero at an ambient temperature, and it increases only weakly to the maximum of less than mass fraction of 0.5% close to the melting point of pure Al. Cr has on the lowest diffusion coefficient from technically important metals and thus it has also a capability to form very fine and stable precipitates. A supersaturated solid solution must be formed before the alloy can be strengthened by artificial ageing. In the Al-Cr system it is only possible via the rapid solidification procedure because the appropriate solubility of Cr is obtained only in the liquid state and it is retained with practical freezing of the melt. For this two RST procesures are possible: inert gas atomizing and melt spinning.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

15th Conference on Materials and Technology

ISBN

978-961-91448-7-9

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

66-67

Název nakladatele

Inštitut za kovinske materiale in technologije

Místo vydání

Ljubljana

Místo konání akce

Portorož

Datum konání akce

8. 10. 2007

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—