Structural changes in Cr-V ledeburitic steel during austenitizing and quenching
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F10%3A00171547" target="_blank" >RIV/68407700:21220/10:00171547 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Structural changes in Cr-V ledeburitic steel during austenitizing and quenching
Popis výsledku v původním jazyce
The Vanadis 6 PM Cr-V ledeburitic steel was austenitized at temperatures from the range 1000 - 1200 oC and nitrogen gas quenched. Structural changes were investigated by light microscopy and SEM. Obtained result fixed that the M7C3-carbides underwent a complete dissolution in the austenite while MC-phase remained almost completely unaffected. The saturation of the austenite by chromium and partly vanadium induced formation of increased portion of non-martensitic structural components after quenching, due to decrease of MS and Mf temperatures. Undissolved part of MC-carbides, located mainly on the grain boundaries, hinders effectively the grains coarsening also at higher austenitizing temperatures.
Název v anglickém jazyce
Structural changes in Cr-V ledeburitic steel during austenitizing and quenching
Popis výsledku anglicky
The Vanadis 6 PM Cr-V ledeburitic steel was austenitized at temperatures from the range 1000 - 1200 oC and nitrogen gas quenched. Structural changes were investigated by light microscopy and SEM. Obtained result fixed that the M7C3-carbides underwent a complete dissolution in the austenite while MC-phase remained almost completely unaffected. The saturation of the austenite by chromium and partly vanadium induced formation of increased portion of non-martensitic structural components after quenching, due to decrease of MS and Mf temperatures. Undissolved part of MC-carbides, located mainly on the grain boundaries, hinders effectively the grains coarsening also at higher austenitizing temperatures.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JJ - Ostatní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
O - Projekt operacniho programu
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Engineering
ISSN
1335-0803
e-ISSN
—
Svazek periodika
17
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
10
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—