Evaluation of structural changes in Cr-V ledeburitic tool steels depending on temperature austenitization
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F11%3A00186952" target="_blank" >RIV/68407700:21220/11:00186952 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Evaluation of structural changes in Cr-V ledeburitic tool steels depending on temperature austenitization
Popis výsledku v původním jazyce
Samples of Vanadis 6 PM Cr-V ledeburitic steel were austenitized at temperatures in the range 1000 - 1200 °C and oil-quenched. The structural changes were investigated by scanning electron microscope and evaluated using NIS Elements software. The obtained results indicated that the M7C3 - carbides underwent intensive dissolution in austenite and were not detected above a temperature of 1100 °C. On the other hand, MC - carbides remained almost completely unaffected and symptoms of dissolution were foundonly at a temperature of 1200 °C. The saturation of the austenite by carbon, chromium and partly also vanadium increased the hardness of the as-quenched material, with the maximum at an austenitizing temperature of 1025 °C.
Název v anglickém jazyce
Evaluation of structural changes in Cr-V ledeburitic tool steels depending on temperature austenitization
Popis výsledku anglicky
Samples of Vanadis 6 PM Cr-V ledeburitic steel were austenitized at temperatures in the range 1000 - 1200 °C and oil-quenched. The structural changes were investigated by scanning electron microscope and evaluated using NIS Elements software. The obtained results indicated that the M7C3 - carbides underwent intensive dissolution in austenite and were not detected above a temperature of 1100 °C. On the other hand, MC - carbides remained almost completely unaffected and symptoms of dissolution were foundonly at a temperature of 1200 °C. The saturation of the austenite by carbon, chromium and partly also vanadium increased the hardness of the as-quenched material, with the maximum at an austenitizing temperature of 1025 °C.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JJ - Ostatní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/FR-TI1%2F003" target="_blank" >FR-TI1/003: Zvýšení životnosti nástrojů z ledeburitických ocelí kryogenním zpracováním</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials and Technology
ISSN
1580-2949
e-ISSN
—
Svazek periodika
45
Číslo periodika v rámci svazku
5
Stát vydavatele periodika
SI - Slovinská republika
Počet stran výsledku
5
Strana od-do
489-493
Kód UT WoS článku
000296487700018
EID výsledku v databázi Scopus
—