Investigation on residual stress profiles and microhardness on Ti6Al4V alloy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F17%3A00320563" target="_blank" >RIV/68407700:21220/17:00320563 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Investigation on residual stress profiles and microhardness on Ti6Al4V alloy
Popis výsledku v původním jazyce
The contribution is dedicated to surface integrity assessment of titanium Ti6Al4V from the point of view of residual stress profile and microhardness profile. Residual stresses play the key role for dynamic life and service reliability of the part, especially rotating aircraft airfoils made of titanium and nickel base alloys. Except a brief summary of measurement methods practical experience with application of Beam deflection method combined with electrolytic etching is published. Specific measurement results for Ti6Al4V coupons finished by face milling, shotpeening and laserpeening are the subject of experimental part.
Název v anglickém jazyce
Investigation on residual stress profiles and microhardness on Ti6Al4V alloy
Popis výsledku anglicky
The contribution is dedicated to surface integrity assessment of titanium Ti6Al4V from the point of view of residual stress profile and microhardness profile. Residual stresses play the key role for dynamic life and service reliability of the part, especially rotating aircraft airfoils made of titanium and nickel base alloys. Except a brief summary of measurement methods practical experience with application of Beam deflection method combined with electrolytic etching is published. Specific measurement results for Ti6Al4V coupons finished by face milling, shotpeening and laserpeening are the subject of experimental part.
Klasifikace
Druh
O - Ostatní výsledky
CEP obor
—
OECD FORD obor
20302 - Applied mechanics
Návaznosti výsledku
Projekt
—
Návaznosti
N - Vyzkumna aktivita podporovana z neverejnych zdroju
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů