The Boron Solubility in Al-Mg-B Alloys
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F24%3A00379427" target="_blank" >RIV/68407700:21220/24:00379427 - isvavai.cz</a>
Výsledek na webu
<a href="https://doi.org/10.24425/afe.2024.151305" target="_blank" >https://doi.org/10.24425/afe.2024.151305</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.24425/afe.2024.151305" target="_blank" >10.24425/afe.2024.151305</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The Boron Solubility in Al-Mg-B Alloys
Popis výsledku v původním jazyce
This study deals with the effect of magnesium content in Al-Mg-B alloy (with a boron content of about 5 wt. %) on the formation of intermetallic phases and elimination of inclusions in the form of boron powder particles in the final structure. At first look, the high melting temperature difference between pure aluminium (660 °C) and boron (2 076 °C) appears to be a potential problem. Moreover, boron has a minimal solubility in aluminium (0.055 wt.%) and the liquidus temperature increases very rapidly with increasing boron content (liquidus temperature approx. 1 160 °C at 5 wt.% for Al-B binary alloy). Alloying with magnesium results in the transformation of the intermetallic phases AlB12 and AlB2 to the (Al, Mg)B2 phase and has a significant beneficial effect on the formation of intermetallic boron phases in the aluminium alloy without residual boron powder particles.
Název v anglickém jazyce
The Boron Solubility in Al-Mg-B Alloys
Popis výsledku anglicky
This study deals with the effect of magnesium content in Al-Mg-B alloy (with a boron content of about 5 wt. %) on the formation of intermetallic phases and elimination of inclusions in the form of boron powder particles in the final structure. At first look, the high melting temperature difference between pure aluminium (660 °C) and boron (2 076 °C) appears to be a potential problem. Moreover, boron has a minimal solubility in aluminium (0.055 wt.%) and the liquidus temperature increases very rapidly with increasing boron content (liquidus temperature approx. 1 160 °C at 5 wt.% for Al-B binary alloy). Alloying with magnesium results in the transformation of the intermetallic phases AlB12 and AlB2 to the (Al, Mg)B2 phase and has a significant beneficial effect on the formation of intermetallic boron phases in the aluminium alloy without residual boron powder particles.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20301 - Mechanical engineering
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2024
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Archives of Foundry Engineering
ISSN
1897-3310
e-ISSN
2299-2944
Svazek periodika
24
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
PL - Polská republika
Počet stran výsledku
6
Strana od-do
15-20
Kód UT WoS článku
001382226800001
EID výsledku v databázi Scopus
2-s2.0-85218501315