Optické vlasntosti Epoxy Novolak Resinu s dotací Dy3+

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21230%2F08%3A03147368" target="_blank" >RIV/68407700:21230/08:03147368 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/60461373:22310/08:00020127 RIV/67985882:_____/08:00346118 RIV/68407700:21230/08:00145466

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Optical Properties of Dy3+ Doped Epoxy Novolak Resin

Popis výsledku v původním jazyce

We report about properties of epoxy novolak resin polymer doped with dysprosium ions. The polymer layers were fabricated by spin-coated onto silicon substrates, or pouring epoxy novolak resin solution into bottomless molds placed on a quartz substrate and leaving them to dry. Infrared spectroscopy was used for investigation of O-H vibrations and we observed absorption band about 3390 cm-1 corresponds to these vibrations. Optical band gap Eg has been determined from the absorption coefficient values using Tauc's procedure, i.e. from the relationship ?hv = A(hv - Eg)2. The optical band gap Eg varied from 3.489 eV to 3.539 eV depends on content of dysprosium ions. Photoluminescence spectra around 1300 nm were investigated by using excitation of He-Ne laser operating at 632.8 nm and two semiconductor lasers operating at 980 nm and 827 nm.

Název v anglickém jazyce

Optical Properties of Dy3+ Doped Epoxy Novolak Resin

Popis výsledku anglicky

We report about properties of epoxy novolak resin polymer doped with dysprosium ions. The polymer layers were fabricated by spin-coated onto silicon substrates, or pouring epoxy novolak resin solution into bottomless molds placed on a quartz substrate and leaving them to dry. Infrared spectroscopy was used for investigation of O-H vibrations and we observed absorption band about 3390 cm-1 corresponds to these vibrations. Optical band gap Eg has been determined from the absorption coefficient values using Tauc's procedure, i.e. from the relationship ?hv = A(hv - Eg)2. The optical band gap Eg varied from 3.489 eV to 3.539 eV depends on content of dysprosium ions. Photoluminescence spectra around 1300 nm were investigated by using excitation of He-Ne laser operating at 632.8 nm and two semiconductor lasers operating at 980 nm and 827 nm.

Druh

D - Stať ve sborníku

CEP obor

JA - Elektronika a optoelektronika, elektrotechnika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA102%2F06%2F0424" target="_blank" >GA102/06/0424: Nové součástky integrované optiky zhotovené planární hybridní technologií</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of SPIE 7061 - Novel Optical Systems Design and Optimization XI

ISBN

978-0-8194-7281-6

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

—

Název nakladatele

SPIE

Místo vydání

Bellingham (stát Washington)

Místo konání akce

San Diego

Datum konání akce

10. 8. 2008

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—