Tribological behaviour of C-alloyed transition metal dichalcogenides (TMD) coatings in different environments

Popis výsledku v původním jazyce

W-S-C films were deposited by non-reactive sputtering from a carbon target incrusted with WS2 pellets in the eroded zone. This process allows depositing coatings with a wide range of compositions, with a precise control of their carbon content. Before the deposition, a Ti interlayer was interposed between the film and the substrate to improve the final adhesion. The carbon content in W-S-C system was varied from 29 at.% to 70 at.%, which led to an hardness enhancement from 4 GPa up to 10 GPa where the maximum hardness was reached in films with a carbon content between 40 at.% and 50 at.%. The tribological behaviour of the coatings was evaluated by pin-on-disk testing, in environments with different humidity levels.

Název v anglickém jazyce

Tribological behaviour of C-alloyed transition metal dichalcogenides (TMD) coatings in different environments

Popis výsledku anglicky

W-S-C films were deposited by non-reactive sputtering from a carbon target incrusted with WS2 pellets in the eroded zone. This process allows depositing coatings with a wide range of compositions, with a precise control of their carbon content. Before the deposition, a Ti interlayer was interposed between the film and the substrate to improve the final adhesion. The carbon content in W-S-C system was varied from 29 at.% to 70 at.%, which led to an hardness enhancement from 4 GPa up to 10 GPa where the maximum hardness was reached in films with a carbon content between 40 at.% and 50 at.%. The tribological behaviour of the coatings was evaluated by pin-on-disk testing, in environments with different humidity levels.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GP106%2F07%2FP014" target="_blank" >GP106/07/P014: Samomazné vrstvy na bázi dichalkogenidů přechodových kovů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

International Journal of Mechanics and Materials in Design

ISSN

1569-1713

e-ISSN

—

Svazek periodika

4

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

7

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—