Atmospheric-Air Plasma Surface Modification of Polyethylene Powder

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21230%2F09%3A00154854" target="_blank" >RIV/68407700:21230/09:00154854 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/46747885:24210/09:#0001111

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Atmospheric-Air Plasma Surface Modification of Polyethylene Powder

Popis výsledku v původním jazyce

Paper describes investigation of polyethylene powder modification using plasma reactor exploiting the dielectric barrier discharge burning in air at atmospheric pressure and ambient temperature. For the test modification the polyethylene powder was used.Effectivity of the modification process was successfully tested by ESCA scans that proved formation of new functional groups at the modified powder surface. Modification effect was also evaluated by means of dynamic capillarity rising measurements. Powder capillarity tests proved significant powder capillarity changes. Modification effect reduction was small (max. reduction about 20% during 1100 days after the modification date), hence modification effect is also very time stable.

Název v anglickém jazyce

Atmospheric-Air Plasma Surface Modification of Polyethylene Powder

Popis výsledku anglicky

Paper describes investigation of polyethylene powder modification using plasma reactor exploiting the dielectric barrier discharge burning in air at atmospheric pressure and ambient temperature. For the test modification the polyethylene powder was used.Effectivity of the modification process was successfully tested by ESCA scans that proved formation of new functional groups at the modified powder surface. Modification effect was also evaluated by means of dynamic capillarity rising measurements. Powder capillarity tests proved significant powder capillarity changes. Modification effect reduction was small (max. reduction about 20% during 1100 days after the modification date), hence modification effect is also very time stable.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BL - Fyzika plasmatu a výboje v plynech

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Plasma Processes and Polymers

ISSN

1612-8850

e-ISSN

—

Svazek periodika

6

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

6

Strana od-do

—

Kód UT WoS článku

000263636200008

EID výsledku v databázi Scopus

—