Silica Encapsulated Manganese Perovskite Nanoparticles for Magnetically Induced Hyperthermia without the Risk of Overheating
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21230%2F09%3A00157499" target="_blank" >RIV/68407700:21230/09:00157499 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68378271:_____/09:00332064 RIV/61388980:_____/09:00332064
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Silica Encapsulated Manganese Perovskite Nanoparticles for Magnetically Induced Hyperthermia without the Risk of Overheating
Popis výsledku v původním jazyce
Manganese perovskite nanoparticles of the composition La0.75Sr0.25MnO3 uniformly coated with silica were prepared by encapsulation of the magnetic cores (mean crystallite size 24 nm) using tetraethoxysilane followed by fractionation. Resulting hybrid particles form a stable suspension in aqueous environmentat at physiological pH and posses a narrow hydrodynamic size distribution. Both calorimetric heating experiments and hysteresis loops in the alternating field revealed high specific power losses, further enhanced by the encapsulation procedure in the case of the coated particles. The corresponding results are discussed on the basis of complex characterization of the particles and especially detailed magnetic measurements. Moreover the Curie temperature (335 K) of the selected magnetic cores resolves the risk of local overheating during hyperthermia treatment.
Název v anglickém jazyce
Silica Encapsulated Manganese Perovskite Nanoparticles for Magnetically Induced Hyperthermia without the Risk of Overheating
Popis výsledku anglicky
Manganese perovskite nanoparticles of the composition La0.75Sr0.25MnO3 uniformly coated with silica were prepared by encapsulation of the magnetic cores (mean crystallite size 24 nm) using tetraethoxysilane followed by fractionation. Resulting hybrid particles form a stable suspension in aqueous environmentat at physiological pH and posses a narrow hydrodynamic size distribution. Both calorimetric heating experiments and hysteresis loops in the alternating field revealed high specific power losses, further enhanced by the encapsulation procedure in the case of the coated particles. The corresponding results are discussed on the basis of complex characterization of the particles and especially detailed magnetic measurements. Moreover the Curie temperature (335 K) of the selected magnetic cores resolves the risk of local overheating during hyperthermia treatment.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Nanotechnology
ISSN
0957-4484
e-ISSN
—
Svazek periodika
2009
Číslo periodika v rámci svazku
20
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
7
Strana od-do
—
Kód UT WoS článku
000267089600022
EID výsledku v databázi Scopus
—