Tribological behaviour a-C and a-C:H films doped with Ti in biological solutions
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21230%2F11%3A00180835" target="_blank" >RIV/68407700:21230/11:00180835 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.vacuum.2011.03.011" target="_blank" >http://dx.doi.org/10.1016/j.vacuum.2011.03.011</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.vacuum.2011.03.011" target="_blank" >10.1016/j.vacuum.2011.03.011</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Tribological behaviour a-C and a-C:H films doped with Ti in biological solutions
Popis výsledku v původním jazyce
The coatings were deposited in a multi magnetron Teer sputtering device with two C targets and a Ti target in Ar atmosphere, on steel and Si substrates. To deposit hydrogenated coatings methane was introduced in the discharge atmosphere. The films were deposited in a range of 7e14 at.% Ti content. X-ray diffraction patterns revealed the presence of a nanocrystalline TiC phase. The hardness varied from 8 to 9 GPa. The tribological tests were performed under dry sliding and lubricated (0.9% NaCl water solution, physiological solution, PS, and 10% fetal bovine serum dissolved in Ringer's saline solution, FBS) conditions, using a 100Cr6 steel balls with a diameter of 6 mm, in a pin-on-disc wear test apparatus.
Název v anglickém jazyce
Tribological behaviour a-C and a-C:H films doped with Ti in biological solutions
Popis výsledku anglicky
The coatings were deposited in a multi magnetron Teer sputtering device with two C targets and a Ti target in Ar atmosphere, on steel and Si substrates. To deposit hydrogenated coatings methane was introduced in the discharge atmosphere. The films were deposited in a range of 7e14 at.% Ti content. X-ray diffraction patterns revealed the presence of a nanocrystalline TiC phase. The hardness varied from 8 to 9 GPa. The tribological tests were performed under dry sliding and lubricated (0.9% NaCl water solution, physiological solution, PS, and 10% fetal bovine serum dissolved in Ringer's saline solution, FBS) conditions, using a 100Cr6 steel balls with a diameter of 6 mm, in a pin-on-disc wear test apparatus.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JI - Kompositní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GAP108%2F10%2F1782" target="_blank" >GAP108/10/1782: Stabilita bioaktivních vrstevnatých struktur v modelových tělních tekutinách.</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Vacuum
ISSN
0042-207X
e-ISSN
—
Svazek periodika
85
Číslo periodika v rámci svazku
12
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
5
Strana od-do
1144-1148