Repetitive nano-impact tests as a new tool to measure fracture toughness in brittle materials

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21230%2F16%3A00303445" target="_blank" >RIV/68407700:21230/16:00303445 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2016.04.026" target="_blank" >http://dx.doi.org/10.1016/j.jeurceramsoc.2016.04.026</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2016.04.026" target="_blank" >10.1016/j.jeurceramsoc.2016.04.026</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Repetitive nano-impact tests as a new tool to measure fracture toughness in brittle materials

Popis výsledku v původním jazyce

Along this work, the feasibility of using repetitive-impact tests with a cube-corner tip and low loads for obtaining quantitative fracture toughness values will be shown. It will be displayed that the impacts are able to produce a cracking similar to the pattern developed for the classical fracture toughness tests in structural ceramics. Moreover, it will be shown how it is possible to identify the crack geometry evolution from Palmqvist crack to half-penny crack with each new impact being able to study the proper evolution of fracture toughness in terms of different indentation models and as a function of the strain rate, ε. Fracture toughness values of Al2O3 descend from ~6.10 MPam (ε=103s-1), to ~3.52 MPam (ε=10-3s-1). These values correspond to those found in the literature for α-Al2O3 demonstrating that the use of repetitive-nano-impact tests provides good reproducibility, high accuracy for reliable fracture toughness testing.

Název v anglickém jazyce

Repetitive nano-impact tests as a new tool to measure fracture toughness in brittle materials

Popis výsledku anglicky

Along this work, the feasibility of using repetitive-impact tests with a cube-corner tip and low loads for obtaining quantitative fracture toughness values will be shown. It will be displayed that the impacts are able to produce a cracking similar to the pattern developed for the classical fracture toughness tests in structural ceramics. Moreover, it will be shown how it is possible to identify the crack geometry evolution from Palmqvist crack to half-penny crack with each new impact being able to study the proper evolution of fracture toughness in terms of different indentation models and as a function of the strain rate, ε. Fracture toughness values of Al2O3 descend from ~6.10 MPam (ε=103s-1), to ~3.52 MPam (ε=10-3s-1). These values correspond to those found in the literature for α-Al2O3 demonstrating that the use of repetitive-nano-impact tests provides good reproducibility, high accuracy for reliable fracture toughness testing.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GP14-32801P" target="_blank" >GP14-32801P: Nový způsob přípravy metalických vrstev pro aplikace v medicíně</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the European Ceramic Society

ISSN

0955-2219

e-ISSN

—

Svazek periodika

36

Číslo periodika v rámci svazku

13

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

9

Strana od-do

3235-3243

Kód UT WoS článku

000378449100018

EID výsledku v databázi Scopus

2-s2.0-84971343032