Competing mechanisms on the strength of ion-irradiated Zr/Nb nanoscale multilayers: Interface strength versus radiation hardening

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21230%2F18%3A00321629" target="_blank" >RIV/68407700:21230/18:00321629 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21340/18:00321629

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.scriptamat.2018.03.039" target="_blank" >http://dx.doi.org/10.1016/j.scriptamat.2018.03.039</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.scriptamat.2018.03.039" target="_blank" >10.1016/j.scriptamat.2018.03.039</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Competing mechanisms on the strength of ion-irradiated Zr/Nb nanoscale multilayers: Interface strength versus radiation hardening

Popis výsledku v původním jazyce

The structural stability and mechanical properties of sputter-deposited Zr/Nb nanoscale multilayers subjected to Si-ion irradiation were investigated in relation to the individual layer thickness. The interface density distribution played a major role on the nature and amount of accumulated radiation damage. The multilayer with a smaller periodicity experienced a significantly higher atomic-scale disorder and radiation hardening compared to the multilayer with thicker individual layers. In the latter case, an enhanced radiation damage tolerance was achieved due to the balance between competing deformation mechanisms.

Název v anglickém jazyce

Competing mechanisms on the strength of ion-irradiated Zr/Nb nanoscale multilayers: Interface strength versus radiation hardening

Popis výsledku anglicky

The structural stability and mechanical properties of sputter-deposited Zr/Nb nanoscale multilayers subjected to Si-ion irradiation were investigated in relation to the individual layer thickness. The interface density distribution played a major role on the nature and amount of accumulated radiation damage. The multilayer with a smaller periodicity experienced a significantly higher atomic-scale disorder and radiation hardening compared to the multilayer with thicker individual layers. In the latter case, an enhanced radiation damage tolerance was achieved due to the balance between competing deformation mechanisms.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

<a href="/cs/project/GA17-17921S" target="_blank" >GA17-17921S: Nanomateriály tolerantní vůči radiačnímu poškození - design rozhraní s regenerační schopností</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Scripta Materialia

ISSN

1359-6462

e-ISSN

—

Svazek periodika

152

Číslo periodika v rámci svazku

July

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

5

Strana od-do

31-35

Kód UT WoS článku

000435051400008

EID výsledku v databázi Scopus

2-s2.0-85045246617