Tribological properties of Mo-S-C coating deposited by pulsed d.c. magnetron sputtering

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21230%2F21%3A00350656" target="_blank" >RIV/68407700:21230/21:00350656 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1016/j.wear.2021.203939" target="_blank" >https://doi.org/10.1016/j.wear.2021.203939</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.wear.2021.203939" target="_blank" >10.1016/j.wear.2021.203939</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Tribological properties of Mo-S-C coating deposited by pulsed d.c. magnetron sputtering

Popis výsledku v původním jazyce

Transition metal dichalcogenides such as MoS2 are widely used as solid lubricants for vacuum applications. On the other hand, diamond-like carbon coatings exhibit excellent sliding properties in the ambient environment. Our Mo-S-C coatings deposited by pulsed d.c. sputtering combine both structures to obtain stable properties regardless of the testing conditions. The coatings were studied using HR-TEM and Raman spectroscopy, revealing amorphous nature of the coating. The tribological properties were evaluated by pin-on-disc method. The results showed high lubrication ability in all the testing conditions. HR-TEM and Raman spectroscopy were employed to show the structural characteristics of the wear traces. Our results indicate that the low-friction effect should be attributed to carbon structure re-arrangement since expected wear-induced MoS2 formation was not observed.

Název v anglickém jazyce

Tribological properties of Mo-S-C coating deposited by pulsed d.c. magnetron sputtering

Popis výsledku anglicky

Transition metal dichalcogenides such as MoS2 are widely used as solid lubricants for vacuum applications. On the other hand, diamond-like carbon coatings exhibit excellent sliding properties in the ambient environment. Our Mo-S-C coatings deposited by pulsed d.c. sputtering combine both structures to obtain stable properties regardless of the testing conditions. The coatings were studied using HR-TEM and Raman spectroscopy, revealing amorphous nature of the coating. The tribological properties were evaluated by pin-on-disc method. The results showed high lubrication ability in all the testing conditions. HR-TEM and Raman spectroscopy were employed to show the structural characteristics of the wear traces. Our results indicate that the low-friction effect should be attributed to carbon structure re-arrangement since expected wear-induced MoS2 formation was not observed.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

<a href="/cs/project/EF16_026%2F0008396" target="_blank" >EF16_026/0008396: Nové nanostruktury pro inženýrské aplikace umožněné kombinací moderních technologií a pokročilých simulací</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2021

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Wear

ISSN

0043-1648

e-ISSN

1873-2577

Svazek periodika

480

Číslo periodika v rámci svazku

September

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

10

Strana od-do

1-10

Kód UT WoS článku

000663556700002

EID výsledku v databázi Scopus

2-s2.0-85106611772