Accumulative Roll Bonding of Continuously Cast Al Sheets

Popis výsledku v původním jazyce

The effect of rolling temperature on the quality of roll bonding, grain refinement, and hardness was studied. After two cycles at 200°C, mean grain size of 0.4 to 0.8 um is achieved in AA8006 sheets, but areas with extremely fine grains of 0.1 to 0.3 umin diameter are also found. ARB processing of AA8006 sheet at 350°C results in better bonding but in smaller increase in hardness due to recrystallisation and grain coarsening occurring during heating to 350°C. High purity Al sheets were ARB processed atroom temperature. Positron lifetime measurements reveal a substantial increase of dislocation density after the first cycle and moderate increase with further ARB cycles.

Název v anglickém jazyce

Accumulative Roll Bonding of Continuously Cast Al Sheets

Popis výsledku anglicky

The effect of rolling temperature on the quality of roll bonding, grain refinement, and hardness was studied. After two cycles at 200°C, mean grain size of 0.4 to 0.8 um is achieved in AA8006 sheets, but areas with extremely fine grains of 0.1 to 0.3 umin diameter are also found. ARB processing of AA8006 sheet at 350°C results in better bonding but in smaller increase in hardness due to recrystallisation and grain coarsening occurring during heating to 350°C. High purity Al sheets were ARB processed atroom temperature. Positron lifetime measurements reveal a substantial increase of dislocation density after the first cycle and moderate increase with further ARB cycles.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

V - Vyzkumna aktivita podporovana z jinych verejnych zdroju

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Evolution of Deformation Microstructures in 3D

ISBN

87-550-3362-8

ISSN

0907-0079

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

Risoe National Laboratory

Místo vydání

Roskilde

Místo konání akce

Roskilde

Datum konání akce

6. 9. 2004

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—