Fotoluminiscence Cr3+ iontů v tenkých vrstvách BaxSr1-xTiO3
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F06%3A04126913" target="_blank" >RIV/68407700:21340/06:04126913 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Photoluminescence of Cr3+ Ions in BaxSr1-xTiO3 Thin Films
Popis výsledku v původním jazyce
Photoluminescence spectra of Cr doped BaxSr1-xTiO3 (BST) thin films with the Ba content from x = 0 to 0.84 were investigated for the first time. The thin films with thickness between 200 - 700 nm were deposited on Pt surface of multi-layer Si/SiO2/TiO2/Pt substrate by the hollow cathode plasma jet system. Chromium doping of BST thin films was accompanied by the appearance of photoluminescence consisting of rather pronounced lines peaking at 12 K in the spectral region 1.57 – 1.60 eV in dependenceon Ba content and a wide structured emission extending behind 1.48 eV. We attribute these lines to the zero-phonon transition 2E ---> 4A2 of octahedral coordinated Cr3+ ions in Ti sites and the structured emission to vibronic sidebands. The observed shift of zero-phonon line to higher energies with increasing x is in accordance with behavior of Cr3+ photoluminescence in the pure SrTiO3 and BaTiO3.
Název v anglickém jazyce
Photoluminescence of Cr3+ Ions in BaxSr1-xTiO3 Thin Films
Popis výsledku anglicky
Photoluminescence spectra of Cr doped BaxSr1-xTiO3 (BST) thin films with the Ba content from x = 0 to 0.84 were investigated for the first time. The thin films with thickness between 200 - 700 nm were deposited on Pt surface of multi-layer Si/SiO2/TiO2/Pt substrate by the hollow cathode plasma jet system. Chromium doping of BST thin films was accompanied by the appearance of photoluminescence consisting of rather pronounced lines peaking at 12 K in the spectral region 1.57 – 1.60 eV in dependenceon Ba content and a wide structured emission extending behind 1.48 eV. We attribute these lines to the zero-phonon transition 2E ---> 4A2 of octahedral coordinated Cr3+ ions in Ti sites and the structured emission to vibronic sidebands. The observed shift of zero-phonon line to higher energies with increasing x is in accordance with behavior of Cr3+ photoluminescence in the pure SrTiO3 and BaTiO3.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2006
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Proceedings of the 16th Joint Seminar
ISBN
80-901748-7-6
ISSN
—
e-ISSN
—
Počet stran výsledku
2
Strana od-do
58-59
Název nakladatele
Czechoslovak Association for Crystal Growth
Místo vydání
Prague
Místo konání akce
Valtice
Datum konání akce
12. 9. 2006
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—