Luminescence Spectroscopy of BaxSr1-xTiO3 Thin Films

Popis výsledku v původním jazyce

Photoluminescence spectra of BaxSr1-xTiO3 (BST) thin films with 0 <=x <= 1 were investigated. The thin films with thickness between 200 - 700 nm were deposited on Pt surface of multi-layer Si/SiO2/TiO2/Pt substrate by the hollow cathode plasma jet system. Photoluminescence emission spectra of studied BST thin films revealed broad emission band peaking in the vicinity of 2.1 eV and rather pronounced lines peaking at 12 K in the spectral region 1.57 - 1.60 eV in dependence on Ba content. These lines wereaccompanied by a wide structured emission extending behind 1.48 eV. We attribute these lines to the zero-phonon transition 2E ----> 4A2 of octahedral coordinated Cr3+ ions in Ti sites and the structured emission to vibronic sidebands. The observed shiftof zero-phonon line to higher energies with increasing x is in accordance with behavior of Cr3+ photoluminescence in the pure SrTiO3 and BaTiO3.

Název v anglickém jazyce

Luminescence Spectroscopy of BaxSr1-xTiO3 Thin Films

Popis výsledku anglicky

Photoluminescence spectra of BaxSr1-xTiO3 (BST) thin films with 0 <=x <= 1 were investigated. The thin films with thickness between 200 - 700 nm were deposited on Pt surface of multi-layer Si/SiO2/TiO2/Pt substrate by the hollow cathode plasma jet system. Photoluminescence emission spectra of studied BST thin films revealed broad emission band peaking in the vicinity of 2.1 eV and rather pronounced lines peaking at 12 K in the spectral region 1.57 - 1.60 eV in dependence on Ba content. These lines wereaccompanied by a wide structured emission extending behind 1.48 eV. We attribute these lines to the zero-phonon transition 2E ----> 4A2 of octahedral coordinated Cr3+ ions in Ti sites and the structured emission to vibronic sidebands. The observed shiftof zero-phonon line to higher energies with increasing x is in accordance with behavior of Cr3+ photoluminescence in the pure SrTiO3 and BaTiO3.

Druh

D - Stať ve sborníku

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of Workshop 2007

ISBN

978-80-01-03667-9

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

88-89

Název nakladatele

ČVUT

Místo vydání

Praha

Místo konání akce

Praha

Datum konání akce

19. 2. 2007

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—