Fotoluminiscence tenkých nanodiamantových vrstev
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F06%3A04126916" target="_blank" >RIV/68407700:21340/06:04126916 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Photoluminescence of Thin Nanodiamond Films
Popis výsledku v původním jazyce
Photoluminescence emission and excitation spectra of thin nanocrystalline diamond films were studied within a wide temperature (12 – 300 K) and spectral (220 – 900 nm) region. Nanodiamond films with thickness within 250-1650 nm were grown bymicrowave plasma-enhanced chemical vapor deposition in hydrogen-methane plasma on silicon (100) substrates. Then windows 6x6 mm were opened in substrates by directional etching, leaving perfectly transparent, self-supporting nanodiamond membranes. Typical nanograin sizes have been observed in the range 20-100 nm. Photoluminescence emission spectra of nanodiamond consist of two main broad emission bands peaking near 2.2 and 1.8 eV at 12 K. Spectra depend on preparation conditions of nanodiamond films butthey do not change markedly with temperature. The luminescence mechanism vas suggested.
Název v anglickém jazyce
Photoluminescence of Thin Nanodiamond Films
Popis výsledku anglicky
Photoluminescence emission and excitation spectra of thin nanocrystalline diamond films were studied within a wide temperature (12 – 300 K) and spectral (220 – 900 nm) region. Nanodiamond films with thickness within 250-1650 nm were grown bymicrowave plasma-enhanced chemical vapor deposition in hydrogen-methane plasma on silicon (100) substrates. Then windows 6x6 mm were opened in substrates by directional etching, leaving perfectly transparent, self-supporting nanodiamond membranes. Typical nanograin sizes have been observed in the range 20-100 nm. Photoluminescence emission spectra of nanodiamond consist of two main broad emission bands peaking near 2.2 and 1.8 eV at 12 K. Spectra depend on preparation conditions of nanodiamond films butthey do not change markedly with temperature. The luminescence mechanism vas suggested.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA202%2F05%2F2233" target="_blank" >GA202/05/2233: Tenké vrstvy nanodiamantu: technologie, strukturní a elektronické vlastnosti a bio-sensory</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2006
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Proceedings of the 16th Joint Seminar
ISBN
80-901748-7-6
ISSN
—
e-ISSN
—
Počet stran výsledku
2
Strana od-do
12-13
Název nakladatele
Czechoslovak Association for Crystal Growth
Místo vydání
Prague
Místo konání akce
Valtice
Datum konání akce
12. 9. 2006
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—