The analysis of residual stresses distribution in the castings of turbine blade made of Inconel 713C alloy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F16%3A00305447" target="_blank" >RIV/68407700:21340/16:00305447 - isvavai.cz</a>
Výsledek na webu
<a href="https://yadda.icm.edu.pl/baztech/element/bwmeta1.element.baztech-d96b04ab-f1ef-4f80-85a0-482b80637642" target="_blank" >https://yadda.icm.edu.pl/baztech/element/bwmeta1.element.baztech-d96b04ab-f1ef-4f80-85a0-482b80637642</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.15199/24.2016.5.5" target="_blank" >10.15199/24.2016.5.5</a>
Alternativní jazyky
Jazyk výsledku
polština
Název v původním jazyce
Analiza stanu naprężeń własnych w odlewach łopatek turbiny z nadstopu niklu Inconel 713C
Popis výsledku v původním jazyce
Kryteria doboru i warunki procesu technologicznego determinują stan naprężeń własnych w elementach konstrukcji maszyn i urządzeń. W pracy przedstawiono analizę oddziaływania obróbki wykończeniowej w procesie obróbki strumieniowo-ściernej na stan naprężeń własnych w warstwie wierzchniej precyzyjnych odlewów łopatek turbiny silnika lotniczego. Odlewy wytworzono z nadstopu niklu Inconel 713C metodą wytapianych modeli. Naprężenia własne w warstwie wierzchniej określono metodą dyfrakcji rentgenowskiej sin2ψ. Ustalono, że w warstwie wierzchniej łopatek występują naprężenia ściskające o wartości od -618 MPa do -719 MPa. Nie stwierdzono wpływu liczby operacji obróbki strumieniowo-ściernej na wartość naprężeń własnych w warstwie wierzchniej odlewów na głębokości do 5 μm.
Název v anglickém jazyce
The analysis of residual stresses distribution in the castings of turbine blade made of Inconel 713C alloy
Popis výsledku anglicky
The selection and conditions of technological process determine the level of residual stress in structural parts. The paper presents the analysis of residual stress distribution in the surface layer of aircraft turbine blade castings after abrasive blasting process. The investigated Inconel 713C cast segment was manufactured by lost-wax casting method. The residual stresses were measured using X-ray diffraction – sin2Ψ method. In the surface layer of blades, the measured values of compressive stresses were ranging from -618 MPa to -719 MPa. Their values were not influenced by the number of abrasive blasting operations down to the depth of 5 μm.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Hutnik Wiadomości Hutnicze
ISSN
1230-3534
e-ISSN
—
Svazek periodika
83
Číslo periodika v rámci svazku
5
Stát vydavatele periodika
PL - Polská republika
Počet stran výsledku
4
Strana od-do
219-222
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—