Some Aspects of Short Cracks
Popis výsledku v původním jazyce
By dint of experimental short fatigue crack propagation particulars, new crack growth dependences were inferred to express short crack characteristics which partition the physically small crack regime from the long crack mode. A new microstructural threshold condition was to simulate short fatigue cracks. Elastic-plastic fracture mechanics factors were applied to evolving the empirical model for physically small crack propagation. Grain boundaries in steel are obstacles against crack propagation, namelyin the fatigue course. Methods utilizing crack density and dimensional analysis are employed for the evaluation of effects of grain both the size and boundary resistance. The measurements demonstrate the dependence on grain size being in good compliancewith the outcomes of analysis
Název v anglickém jazyce
Some Aspects of Short Cracks
Popis výsledku anglicky
By dint of experimental short fatigue crack propagation particulars, new crack growth dependences were inferred to express short crack characteristics which partition the physically small crack regime from the long crack mode. A new microstructural threshold condition was to simulate short fatigue cracks. Elastic-plastic fracture mechanics factors were applied to evolving the empirical model for physically small crack propagation. Grain boundaries in steel are obstacles against crack propagation, namelyin the fatigue course. Methods utilizing crack density and dimensional analysis are employed for the evaluation of effects of grain both the size and boundary resistance. The measurements demonstrate the dependence on grain size being in good compliancewith the outcomes of analysis
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JN - Stavebnictví
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA103%2F00%2F0897" target="_blank" >GA103/00/0897: Problém únavy dýchajících stěn ocelových nosníků</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2001
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Acta Metallurgica Slovaca
ISBN
—
ISSN
—
e-ISSN
—
Počet stran výsledku
4
Strana od-do
395-398
Název nakladatele
TU
Místo vydání
Košice
Místo konání akce
Stará Lesná
Datum konání akce
25. 4. 2001
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—