FATIGUE BEHAVIOR OF ULTRA-HIGH PERFORMANCE CONCRETE (UHPC) UNDER COMPRESSIVE LOADING

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21610%2F17%3A00316110" target="_blank" >RIV/68407700:21610/17:00316110 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

FATIGUE BEHAVIOR OF ULTRA-HIGH PERFORMANCE CONCRETE (UHPC) UNDER COMPRESSIVE LOADING

Popis výsledku v původním jazyce

Fatigue behavior of Ultra-High Performance Concrete (UHPC) under compressive loading is investigated in this paper. For suitable design of tower structure of wind turbines, fatigue properties are keys factor to be considered. Two main types of mechanical tests were carried out in this study: static tests for the compressive strength evaluation and fatigue tests under compressive loading. At the applied stress level for the fatigue test (upper stress = 0.6 and lower stress = 0.1), the results show that the UHPC specimens withstand to 10 million cycles of loading. The static tests carried (after fatigue tests) show no deterioration or damage of the specimens and no drop of the maximum compressive stress values compared to specimens tested before fatigue tests. These results lead to conclude that the wind turbines made of UHPC might withstand to the fatigue for 20 years of operating time.

Název v anglickém jazyce

FATIGUE BEHAVIOR OF ULTRA-HIGH PERFORMANCE CONCRETE (UHPC) UNDER COMPRESSIVE LOADING

Popis výsledku anglicky

Fatigue behavior of Ultra-High Performance Concrete (UHPC) under compressive loading is investigated in this paper. For suitable design of tower structure of wind turbines, fatigue properties are keys factor to be considered. Two main types of mechanical tests were carried out in this study: static tests for the compressive strength evaluation and fatigue tests under compressive loading. At the applied stress level for the fatigue test (upper stress = 0.6 and lower stress = 0.1), the results show that the UHPC specimens withstand to 10 million cycles of loading. The static tests carried (after fatigue tests) show no deterioration or damage of the specimens and no drop of the maximum compressive stress values compared to specimens tested before fatigue tests. These results lead to conclude that the wind turbines made of UHPC might withstand to the fatigue for 20 years of operating time.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20101 - Civil engineering

Projekt

<a href="/cs/project/GA17-22796S" target="_blank" >GA17-22796S: Experimentální a numerická analýza soudržnosti kovové výztuže s ultra vysokohodnotným betonem (UHPC) za vysokých teplot</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

C - Předmět řešení projektu podléhá obchodnímu tajemství (§ 504 Občanského zákoníku), ale název projektu, cíle projektu a u ukončeného nebo zastaveného projektu zhodnocení výsledku řešení projektu (údaje P03, P04, P15, P19, P29, PN8) dodané do CEP, jsou upraveny tak, aby byly zveřejnitelné.

Název statě ve sborníku

UHPFRC 2017 Designing and Building with UHPFRC: New large-scale implementations, recent technical advances, experience and standards

ISBN

978-2-35158-166-7

ISSN

—

e-ISSN

—

Počet stran výsledku

10

Strana od-do

291-300

Název nakladatele

Rilem Publications s.a.r.l.

Místo vydání

Bagneux

Místo konání akce

Montpellier

Datum konání akce

2. 10. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—