Effect of beta-Nucleation on Crystallization of Photodegraded Polypropylene
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F09%3A63508723" target="_blank" >RIV/70883521:28110/09:63508723 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of beta-Nucleation on Crystallization of Photodegraded Polypropylene
Popis výsledku v původním jazyce
The work deals with crystallization of photodegraded polypropylene containing various amounts of -nucleating agent based on N,N?-dicyclohexylnaphthalene-2,6-dicarboxamide. Compression-moulded samples were irradiated by UV-light, melted and subsequently non-isothermally crystallized. The results showed that the crystallization temperature decreased with increasing irradiation time. The irradiation caused the splitting of crystallization exotherms into two peaks indicating two crystallization mechanisms.The presence of -nucleating agent in the material suppressed the peak splitting; the higher was the amount of nucleating agent in the sample, the later was the splitting observed.
Název v anglickém jazyce
Effect of beta-Nucleation on Crystallization of Photodegraded Polypropylene
Popis výsledku anglicky
The work deals with crystallization of photodegraded polypropylene containing various amounts of -nucleating agent based on N,N?-dicyclohexylnaphthalene-2,6-dicarboxamide. Compression-moulded samples were irradiated by UV-light, melted and subsequently non-isothermally crystallized. The results showed that the crystallization temperature decreased with increasing irradiation time. The irradiation caused the splitting of crystallization exotherms into two peaks indicating two crystallization mechanisms.The presence of -nucleating agent in the material suppressed the peak splitting; the higher was the amount of nucleating agent in the sample, the later was the splitting observed.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CD - Makromolekulární chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GP106%2F07%2FP262" target="_blank" >GP106/07/P262: Mikrofibrilární polymer-polymer kompozity připravované in-situ</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Thermal Analysis and Calorimetry
ISSN
1388-6150
e-ISSN
—
Svazek periodika
95
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
6
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—