Effect of octene content on thermal and mechanical properties of crosslinked ethylene-octene copolymers
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F14%3A43873131" target="_blank" >RIV/70883521:28110/14:43873131 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of octene content on thermal and mechanical properties of crosslinked ethylene-octene copolymers
Popis výsledku v původním jazyce
Two ethylene-octene copolymers (EOC - with octene wt.% of 20 and 35) were crosslinked using dicumyl peroxide (DCP). Crosslinking studies were done using rubber process analyzer (RPA) at 150-200 oC range. Highest s'<inf>max</inf> (maximum elastic torque)was found for EOC-20 with low octene content, always. High-octene EOC underwent more degradation. From dynamic mechanical analysis (DMA), storage modulus (M') and glass transition temperature (T<inf>g</inf>) were found decreasing with increasing octene content. Differential scanning calorimetry (DSC) revealed the inverse effect of octene content on crystallinity and melting point. For high-octene EOC, increased ?-scission has resulted in the poorer crosslinking and inferior properties.
Název v anglickém jazyce
Effect of octene content on thermal and mechanical properties of crosslinked ethylene-octene copolymers
Popis výsledku anglicky
Two ethylene-octene copolymers (EOC - with octene wt.% of 20 and 35) were crosslinked using dicumyl peroxide (DCP). Crosslinking studies were done using rubber process analyzer (RPA) at 150-200 oC range. Highest s'<inf>max</inf> (maximum elastic torque)was found for EOC-20 with low octene content, always. High-octene EOC underwent more degradation. From dynamic mechanical analysis (DMA), storage modulus (M') and glass transition temperature (T<inf>g</inf>) were found decreasing with increasing octene content. Differential scanning calorimetry (DSC) revealed the inverse effect of octene content on crystallinity and melting point. For high-octene EOC, increased ?-scission has resulted in the poorer crosslinking and inferior properties.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
CD - Makromolekulární chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
V - Vyzkumna aktivita podporovana z jinych verejnych zdroju
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Technical Conference and Exhibition of the Society of Plastics Engineers (ANTEC DUBAI 2014)
ISBN
978-1-63439-717-9
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
44-49
Název nakladatele
Society of Plastics Engineers ( SPE )
Místo vydání
Brookfield
Místo konání akce
Dubai
Datum konání akce
21. 1. 2014
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—