Effect of length of glass fibers in recycled polypropylene on mechanical properties
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28140%2F16%3A43874630" target="_blank" >RIV/70883521:28140/16:43874630 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/70883521:28110/16:43874630
Výsledek na webu
<a href="http://www.mmscience.eu/october-2016.html" target="_blank" >http://www.mmscience.eu/october-2016.html</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.17973/MMSJ.2016_10_201679" target="_blank" >10.17973/MMSJ.2016_10_201679</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of length of glass fibers in recycled polypropylene on mechanical properties
Popis výsledku v původním jazyce
This article investigates the effect of recycled material particle size on the resulting mechanical properties of products. The product material was polypropylene with glass fibers. Recycled material was prepared by mechanical way of recyclation, then it was categorized by sieve analysis to different size of particles. After preparation, the samples were subjugated to mechanical tests. The samples were subjected to the Charpy impact test, the hardness of Shore D test. Testing was conducted at ambient temperatures. The effect of reprocessing of the material is mainly represented by fiber shortening. As a result, considerable reduction of mechanical properties can be observed.
Název v anglickém jazyce
Effect of length of glass fibers in recycled polypropylene on mechanical properties
Popis výsledku anglicky
This article investigates the effect of recycled material particle size on the resulting mechanical properties of products. The product material was polypropylene with glass fibers. Recycled material was prepared by mechanical way of recyclation, then it was categorized by sieve analysis to different size of particles. After preparation, the samples were subjugated to mechanical tests. The samples were subjected to the Charpy impact test, the hardness of Shore D test. Testing was conducted at ambient temperatures. The effect of reprocessing of the material is mainly represented by fiber shortening. As a result, considerable reduction of mechanical properties can be observed.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JP - Průmyslové procesy a zpracování
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/ED2.1.00%2F03.0089" target="_blank" >ED2.1.00/03.0089: Centrum bezpečnostních, informačních a pokročilých technologií (CEBIA-Tech)</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
MM Science Journal
ISSN
1803-1269
e-ISSN
—
Svazek periodika
2016
Číslo periodika v rámci svazku
OCTOBER
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
4
Strana od-do
1114-1117
Kód UT WoS článku
—
EID výsledku v databázi Scopus
2-s2.0-84988810040