Cryogenic Milling of Titanium Powder
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F18%3A10389179" target="_blank" >RIV/00216208:11320/18:10389179 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61389021:_____/18:00490727
Výsledek na webu
<a href="https://doi.org/10.3390/met8010031" target="_blank" >https://doi.org/10.3390/met8010031</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.3390/met8010031" target="_blank" >10.3390/met8010031</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Cryogenic Milling of Titanium Powder
Popis výsledku v původním jazyce
Ti Grade 2 was prepared by cryogenic attritor milling in liquid nitrogen and liquid argon. Two types of milling balls were used-stainless steel balls and heavy tungsten carbide balls. The effect of processing parameters on particle size and morphology, contamination of powder and its microhardness was investigated. Milling in liquid nitrogen was not feasible due to excessive contamination by nitrogen. Minor reduction of particle size and significant alterations in particle morphology depended on type of milling balls and application of stearic acid as processing control agent. Heavily deformed ultra-fine grained (UFG) internal microstructure of powder particles was observed by the method of "transmission Kikuchi diffraction".
Název v anglickém jazyce
Cryogenic Milling of Titanium Powder
Popis výsledku anglicky
Ti Grade 2 was prepared by cryogenic attritor milling in liquid nitrogen and liquid argon. Two types of milling balls were used-stainless steel balls and heavy tungsten carbide balls. The effect of processing parameters on particle size and morphology, contamination of powder and its microhardness was investigated. Milling in liquid nitrogen was not feasible due to excessive contamination by nitrogen. Minor reduction of particle size and significant alterations in particle morphology depended on type of milling balls and application of stearic acid as processing control agent. Heavily deformed ultra-fine grained (UFG) internal microstructure of powder particles was observed by the method of "transmission Kikuchi diffraction".
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
10302 - Condensed matter physics (including formerly solid state physics, supercond.)
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Metals
ISSN
2075-4701
e-ISSN
—
Svazek periodika
8
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
12
Strana od-do
—
Kód UT WoS článku
000427529100031
EID výsledku v databázi Scopus
2-s2.0-85041428919