Surface analysis of metal nanoparticles by means of Knudsen effusion mass spectrometry
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F13%3A00071227" target="_blank" >RIV/00216224:14310/13:00071227 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Surface analysis of metal nanoparticles by means of Knudsen effusion mass spectrometry
Popis výsledku v původním jazyce
Metal nanoparticles are considered as potential candidates for use in many industrial areas. One of them is the field of solder materials for high temperature applications. Main problem of lead-free solder materials is surface oxidation or reactions which decrease for example the wettability of the solder. Study of surface effects and thermal stability of these small objects is, therefore, of a great importance. Surface effects taking place during thermal analysis of various metal nanoparticles on the basis of surface analysis by Knudsen effusion mass spectrometry were, therefore, studied.
Název v anglickém jazyce
Surface analysis of metal nanoparticles by means of Knudsen effusion mass spectrometry
Popis výsledku anglicky
Metal nanoparticles are considered as potential candidates for use in many industrial areas. One of them is the field of solder materials for high temperature applications. Main problem of lead-free solder materials is surface oxidation or reactions which decrease for example the wettability of the solder. Study of surface effects and thermal stability of these small objects is, therefore, of a great importance. Surface effects taking place during thermal analysis of various metal nanoparticles on the basis of surface analysis by Knudsen effusion mass spectrometry were, therefore, studied.
Klasifikace
Druh
O - Ostatní výsledky
CEP obor
CF - Fyzikální chemie a teoretická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/LD11046" target="_blank" >LD11046: Fázové diagramy nanoslitin, jejich výpočty a ověření.</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů