Thermoelectric properties of Bi2O2Se
Popis výsledku v původním jazyce
Bi2O2Se was synthesized from Bi2Se3 and Bi2O3 by solid state reaction in an evacuated quartz ampoule. The product crystallizes in the tetragonal type lattice and X-ray pattern displays lines of the Bi2O2Se only. Samples for thermoelectric property measurements were prepared using hot pressing in rectangular graphite dies. The samples were characterized by the measurements of Seebeck coefficient, electrical conductivity and thermal conductivity as a function of temperature. From the experimental data wecalculate the dimensionless figure of merit ZT that for a non-optimized material approaches the value 0.2 at 800 K.
Název v anglickém jazyce
Thermoelectric properties of Bi2O2Se
Popis výsledku anglicky
Bi2O2Se was synthesized from Bi2Se3 and Bi2O3 by solid state reaction in an evacuated quartz ampoule. The product crystallizes in the tetragonal type lattice and X-ray pattern displays lines of the Bi2O2Se only. Samples for thermoelectric property measurements were prepared using hot pressing in rectangular graphite dies. The samples were characterized by the measurements of Seebeck coefficient, electrical conductivity and thermal conductivity as a function of temperature. From the experimental data wecalculate the dimensionless figure of merit ZT that for a non-optimized material approaches the value 0.2 at 800 K.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—

Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)