Alkalicky aktivované aluminosilitátové kompozity jako ohnivzdorné materiály

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F08%3APU74471" target="_blank" >RIV/00216305:26110/08:PU74471 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

ALKALI ACTIVATED ALUMINOSILICATE COMPOSITES AS FIRE RESISTANT MATERIALS

Popis výsledku v původním jazyce

Portland cement concrete is the most common and widespread material for constructions. However, its undesirable fast degradation, when exposed to very high temperature, connected with compressive strength decrease, cracking and spalling limits the utilization of concrete in constructions endangered by fire. This paper deals with the properties of alkali activated aluminosilicate materials and a possibility of their utilization as fire protection. These materials are more resistant against high temperatures, especially against shock loading, than Portland cement concrete. In the experiments we examined and compared the behaviour and properties of concrete specimens made from Portland cement and alkali activated slag after treatment at temperatures from200 to 1200 C. The influence of aggregates, comparing quartz sand and electrical porcelain, was also examined.

Název v anglickém jazyce

ALKALI ACTIVATED ALUMINOSILICATE COMPOSITES AS FIRE RESISTANT MATERIALS

Popis výsledku anglicky

Portland cement concrete is the most common and widespread material for constructions. However, its undesirable fast degradation, when exposed to very high temperature, connected with compressive strength decrease, cracking and spalling limits the utilization of concrete in constructions endangered by fire. This paper deals with the properties of alkali activated aluminosilicate materials and a possibility of their utilization as fire protection. These materials are more resistant against high temperatures, especially against shock loading, than Portland cement concrete. In the experiments we examined and compared the behaviour and properties of concrete specimens made from Portland cement and alkali activated slag after treatment at temperatures from200 to 1200 C. The influence of aggregates, comparing quartz sand and electrical porcelain, was also examined.

Druh

D - Stať ve sborníku

CEP obor

JN - Stavebnictví

OECD FORD obor

—

Projekt

<a href="/cs/project/1M0579" target="_blank" >1M0579: Centrum integrovaného navrhování progresivních stavebních konstrukcí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Networks for sustainable environment and high quality of life

ISBN

978-953-95428-7-8

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

—

Název nakladatele

SECON

Místo vydání

Zabreg Croatia

Místo konání akce

Dubrovnik

Datum konání akce

23. 5. 2008

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—