Utilisation of alkali activated aluminosilicates as fire protecting materials

Popis výsledku v původním jazyce

Portland cement concrete is the most common and widespread material for constructions. However, its undesirable fast degradation, when exposed to very high temperature, connected with compressive strength decrease, cracking and spalling limits the utilisation of concrete in constructions endangered by fire. This paper deals with a possibility of subsidiary fire protection using a material based on alkali-activated aluminosilicate (AAAS). This material is more resistant against high temperatures, especially against shock loading, than Portland cement concretes. In the experiments we examined and compared the behaviour and properties of concrete specimens made from Portland cement and AAAS after shock treatment at the temperatures of 1000 and 1200 C. Theinfluence of aggregates, comparing quartz sand and electrical porcelain, was also examined.

Název v anglickém jazyce

Utilisation of alkali activated aluminosilicates as fire protecting materials

Popis výsledku anglicky

Portland cement concrete is the most common and widespread material for constructions. However, its undesirable fast degradation, when exposed to very high temperature, connected with compressive strength decrease, cracking and spalling limits the utilisation of concrete in constructions endangered by fire. This paper deals with a possibility of subsidiary fire protection using a material based on alkali-activated aluminosilicate (AAAS). This material is more resistant against high temperatures, especially against shock loading, than Portland cement concretes. In the experiments we examined and compared the behaviour and properties of concrete specimens made from Portland cement and AAAS after shock treatment at the temperatures of 1000 and 1200 C. Theinfluence of aggregates, comparing quartz sand and electrical porcelain, was also examined.

Druh

D - Stať ve sborníku

CEP obor

JN - Stavebnictví

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Concrete for Fire Engineering

ISBN

978-1-84806-041-8

ISSN

—

e-ISSN

—

Počet stran výsledku

10

Strana od-do

—

Název nakladatele

IHs BRE Press

Místo vydání

Brecknell UK

Místo konání akce

Dundee

Datum konání akce

8. 7. 2008

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—