Sintering of bulk zirconia nanoceramics

Popis výsledku v původním jazyce

The sintering and the microstructure of zirconia ceramics prepared by cold isostatic pressing of nanoceramic powders were studied. Ceramic powders contained 0, 1.5 and 3 mol.% of yttria. It was found that higher compacting pressures (700 MPa) yielded green bodies with smaller pores, which showed in their better sinterability. After sintering at 1100°C, the bodies had a density exceeding 90% t.d. and grains below 80 nm. A critical ratio of the pore size in green bodies to the particle size was establisheed, which enables sintering zirconia nanopowders of some 10 nm in size at a temperature of 1100°C.

Název v anglickém jazyce

Sintering of bulk zirconia nanoceramics

Popis výsledku anglicky

The sintering and the microstructure of zirconia ceramics prepared by cold isostatic pressing of nanoceramic powders were studied. Ceramic powders contained 0, 1.5 and 3 mol.% of yttria. It was found that higher compacting pressures (700 MPa) yielded green bodies with smaller pores, which showed in their better sinterability. After sintering at 1100°C, the bodies had a density exceeding 90% t.d. and grains below 80 nm. A critical ratio of the pore size in green bodies to the particle size was establisheed, which enables sintering zirconia nanopowders of some 10 nm in size at a temperature of 1100°C.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/OC%20523.10" target="_blank" >OC 523.10: Syntézy a vlastnosti nanometrických keramických prášků a solů</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2003

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Reviews on Advanced Materials Science

ISSN

1606-5131

e-ISSN

—

Svazek periodika

5

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

RU - Ruská federace

Počet stran výsledku

4

Strana od-do

183-186

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—