Sintering of alumina and zirconia nanoceramics

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F03%3APU41933" target="_blank" >RIV/00216305:26210/03:PU41933 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Sintering of alumina and zirconia nanoceramics

Popis výsledku v původním jazyce

The sintering and the microstructure of alumina and zirconia ceramics prepared by cold isostatic pressing of nanoceramic powders were studied. Ceramic powders contained 0, 1.5 and 3 mol.% of yttria. It was found that higher compacting pressures (700 MPa)yielded green bodies with smaller pores, which showed in their better sinterability. After sintering at 1100°C, the bodies had a density exceeding 90% t.d. and grains below 80 nm. A critical ratio of the pore size in green bodies to the particle size waas established, which enables sintering zirconia nanopowders of some 10 nm in size at a temperature of 1100°C.

Název v anglickém jazyce

Sintering of alumina and zirconia nanoceramics

Popis výsledku anglicky

The sintering and the microstructure of alumina and zirconia ceramics prepared by cold isostatic pressing of nanoceramic powders were studied. Ceramic powders contained 0, 1.5 and 3 mol.% of yttria. It was found that higher compacting pressures (700 MPa)yielded green bodies with smaller pores, which showed in their better sinterability. After sintering at 1100°C, the bodies had a density exceeding 90% t.d. and grains below 80 nm. A critical ratio of the pore size in green bodies to the particle size waas established, which enables sintering zirconia nanopowders of some 10 nm in size at a temperature of 1100°C.

Druh

D - Stať ve sborníku

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/OC%20523.10" target="_blank" >OC 523.10: Syntézy a vlastnosti nanometrických keramických prášků a solů</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2003

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

School of Ceramics, V Students' meeting

ISBN

86-80995-46-0

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

38-39

Název nakladatele

Faculty of Technology, University of Novi Sad

Místo vydání

Novi Sad

Místo konání akce

Novi Sad

Datum konání akce

4. 12. 2003

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—