Compaction and Pressureless Sintering of Zirconia Nanoparticles

Popis výsledku v původním jazyce

Four nanometer-sized zirconia powders stabilized by 3 mol% Y2O3 were used for the preparation of dense bulk ceramics. Ceramic green bodies were prepared by cold isostatic pressing at pressures of 300-1000 MPa. The size of pores in ceramic green bodies and their evolution during sintering were correlated with the characteristics of individual nanopowders and with the sintering behavior of powder compacts. Only homogeneous green bodies with pores of less than 10 nm could be sintered into dense bodies (>99% t.d.) at sufficiently low temperature to keep the grain sizes in a range <100 nm. Powder with uniform particles of 10 nm in size yielded green bodies of required microstructure. These nanoparticle compacts were sintered without pressure to give bodies(diameter 20 mm, thickness 4 mm) with a relative density higher than 99% and a grain size of about 85 nm (as determined by linear intercept method).

Název v anglickém jazyce

Compaction and Pressureless Sintering of Zirconia Nanoparticles

Popis výsledku anglicky

Four nanometer-sized zirconia powders stabilized by 3 mol% Y2O3 were used for the preparation of dense bulk ceramics. Ceramic green bodies were prepared by cold isostatic pressing at pressures of 300-1000 MPa. The size of pores in ceramic green bodies and their evolution during sintering were correlated with the characteristics of individual nanopowders and with the sintering behavior of powder compacts. Only homogeneous green bodies with pores of less than 10 nm could be sintered into dense bodies (>99% t.d.) at sufficiently low temperature to keep the grain sizes in a range <100 nm. Powder with uniform particles of 10 nm in size yielded green bodies of required microstructure. These nanoparticle compacts were sintered without pressure to give bodies(diameter 20 mm, thickness 4 mm) with a relative density higher than 99% and a grain size of about 85 nm (as determined by linear intercept method).

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the American Ceramic Society

ISSN

0002-7820

e-ISSN

—

Svazek periodika

90

Číslo periodika v rámci svazku

9

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

6

Strana od-do

2735-2740

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—