Přemostění a zachycení čela trhliny v borosilikátových sklech s kovovými částicemi.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F04%3APU47495" target="_blank" >RIV/00216305:26210/04:PU47495 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Crack bridging and trapping in borosilicate matrix composites with distributed metal particles

Popis výsledku v původním jazyce

One of the most efficient ways to improve the fracture toughness of ceramics is to reinforce them by large volume fraction of bonded metal particles The toughening effect of the metal particles was attributed to both crack trapping and bridging. While the bridging effect has been relatively well documented, the crack trapping effect is still somewhat inadequately understood. In contrast to crack bridging, the effectiveness of crack trapping increases with the debonding toughness of the particle/matrix interface. When the tough heterogeneities are equiaxed particles, adhesive strength becomes a very critical issue. Specifically, some optimum interface debonding is needed to remove the geometric constraint and allow the particles to deform plasticallyina significant part of their volume. The aim of the contribution is to confront the measured fracture toughness values obtained on borosilicate glass matrix composites with theoretical predictions.

Název v anglickém jazyce

Crack bridging and trapping in borosilicate matrix composites with distributed metal particles

Popis výsledku anglicky

One of the most efficient ways to improve the fracture toughness of ceramics is to reinforce them by large volume fraction of bonded metal particles The toughening effect of the metal particles was attributed to both crack trapping and bridging. While the bridging effect has been relatively well documented, the crack trapping effect is still somewhat inadequately understood. In contrast to crack bridging, the effectiveness of crack trapping increases with the debonding toughness of the particle/matrix interface. When the tough heterogeneities are equiaxed particles, adhesive strength becomes a very critical issue. Specifically, some optimum interface debonding is needed to remove the geometric constraint and allow the particles to deform plasticallyina significant part of their volume. The aim of the contribution is to confront the measured fracture toughness values obtained on borosilicate glass matrix composites with theoretical predictions.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA101%2F02%2F0683" target="_blank" >GA101/02/0683: Chování trhlin/mikrotrhlin ve vybraných kompozitech s křehkou matricí</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

ECF15

ISBN

—

ISSN

—

e-ISSN

—

Počet stran výsledku

9

Strana od-do

185-193

Název nakladatele

NEUVEDEN

Místo vydání

Stockholm

Místo konání akce

Stockholm

Datum konání akce

11. 8. 2004

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—