Crack bridging and trapping in borosilicate matrix composites with distributed metal particles

Popis výsledku v původním jazyce

One of the most efficient ways to improve the fracture toughness of ceramics is to reinforce them by large volume fraction of bonded metal particles (e.g., Krstic [1]; Evans and McMeeking [2]). The toughening effect of the metal particles was attributedto both crack trapping and bridging. While the bridging effect has been relatively well documented, the crack trapping effect is still somewhat inadequately understood. In contrast to crack bridging, the effectiveness of crack trapping increases with thedebonding toughness of the particle/matrix interface. When the tough heterogeneities are equiaxed particles, adhesive strength becomes a very critical issue. Specifically, some optimum interface debonding is needed to remove the geometric constraint andallow the particles to deform plastically in a significant part of their volume. The aim of the contribution is to confront the measured fracture toughness values obtained on borosilicate glass matrix composites with theoretical predi...

Název v anglickém jazyce

Crack bridging and trapping in borosilicate matrix composites with distributed metal particles

Popis výsledku anglicky

One of the most efficient ways to improve the fracture toughness of ceramics is to reinforce them by large volume fraction of bonded metal particles (e.g., Krstic [1]; Evans and McMeeking [2]). The toughening effect of the metal particles was attributedto both crack trapping and bridging. While the bridging effect has been relatively well documented, the crack trapping effect is still somewhat inadequately understood. In contrast to crack bridging, the effectiveness of crack trapping increases with thedebonding toughness of the particle/matrix interface. When the tough heterogeneities are equiaxed particles, adhesive strength becomes a very critical issue. Specifically, some optimum interface debonding is needed to remove the geometric constraint andallow the particles to deform plastically in a significant part of their volume. The aim of the contribution is to confront the measured fracture toughness values obtained on borosilicate glass matrix composites with theoretical predi...

Druh

D - Stať ve sborníku

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GA101%2F02%2F0683" target="_blank" >GA101/02/0683: Chování trhlin/mikrotrhlin ve vybraných kompozitech s křehkou matricí</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

European Conference of Fracture. Advanced Fracture Mechanics for Life and Safety Asessments /15./

ISBN

—

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

1-5

Název nakladatele

Royal Institute of Technology (KTH)

Místo vydání

Stockholm

Místo konání akce

Stockholm

Datum konání akce

11. 8. 2004

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—