Kvantifikace houževnatosti zvýšená vlivem kovových částic v kompozitech se skelnou matricí

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F05%3A00024477" target="_blank" >RIV/68081723:_____/05:00024477 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26210/05:PU55202

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Quantification of Toughness Increase Due to Metal Particles in Glass Matrix Composites

Popis výsledku v původním jazyce

The paper is focused on a calculation procedure that is capable of discerning subtle changes in fracture toughness behaviour of very brittle material reinforced by ductile metallic particle. For experimental verification borosilicate glass matrix reinforced by vanadium particles has been used the fracture toughness being measured by chevron notch technique. Rice's perturbation analysis was used to the configuration of the front of a planar crack that is trapped against forward advance by a periodical array of closely spaced bridges. The model proposed is capable to explain experimental observations concerning the transition from intrinsic toughening controlled by second phase crack trapping to extrinsic toughening controlled by second phase crack bridging even when the ratio Gd to GIC is virtually constant.

Název v anglickém jazyce

Quantification of Toughness Increase Due to Metal Particles in Glass Matrix Composites

Popis výsledku anglicky

The paper is focused on a calculation procedure that is capable of discerning subtle changes in fracture toughness behaviour of very brittle material reinforced by ductile metallic particle. For experimental verification borosilicate glass matrix reinforced by vanadium particles has been used the fracture toughness being measured by chevron notch technique. Rice's perturbation analysis was used to the configuration of the front of a planar crack that is trapped against forward advance by a periodical array of closely spaced bridges. The model proposed is capable to explain experimental observations concerning the transition from intrinsic toughening controlled by second phase crack trapping to extrinsic toughening controlled by second phase crack bridging even when the ratio Gd to GIC is virtually constant.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA101%2F02%2F0683" target="_blank" >GA101/02/0683: Chování trhlin/mikrotrhlin ve vybraných kompozitech s křehkou matricí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Fracture Mechanics of Ceramics

ISBN

0-387-24134-5

ISSN

—

e-ISSN

—

Počet stran výsledku

17

Strana od-do

245-261

Název nakladatele

Springer Science+Business Media, Inc

Místo vydání

New York

Místo konání akce

Houston, Texas

Datum konání akce

25. 2. 2003

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—