Microcrack interaction with a main crack bridged by ductile particles Part I: Colinear Microcrack
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F99%3A00000033" target="_blank" >RIV/00216305:26210/99:00000033 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Microcrack interaction with a main crack bridged by ductile particles Part I: Colinear Microcrack
Popis výsledku v původním jazyce
The fracture problem for a brittle matrix reinforced by ductile particles is considered. In the usual manner it is assumed that the crack surface bridging forces provided by the unbroken particles improve the fracture toughness of the matrix. Moreover, asingle collinear microcrack on a continuation of the main crack is considered. Such a configuration of the microcrack shows a deleterious effect on fracture toughness. Consequently, it is of interest to study theoretically the interaction between a main, bridged crack and neighbouring microcrack. While partial problems were already solved and amply reported in literature, the combined toughening effect of crack bridging and induced microcracking is still not adequately und
Název v anglickém jazyce
Microcrack interaction with a main crack bridged by ductile particles Part I: Colinear Microcrack
Popis výsledku anglicky
The fracture problem for a brittle matrix reinforced by ductile particles is considered. In the usual manner it is assumed that the crack surface bridging forces provided by the unbroken particles improve the fracture toughness of the matrix. Moreover, asingle collinear microcrack on a continuation of the main crack is considered. Such a configuration of the microcrack shows a deleterious effect on fracture toughness. Consequently, it is of interest to study theoretically the interaction between a main, bridged crack and neighbouring microcrack. While partial problems were already solved and amply reported in literature, the combined toughening effect of crack bridging and induced microcracking is still not adequately und
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA101%2F99%2F0829" target="_blank" >GA101/99/0829: Mikromechanika a nefenomenologické konstitutivní modely kompozitů s křehkou matricí v podmínkách víceosého nízkocyklického tlakového zatěžování</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
1999
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Inženýrská mechanika
ISSN
1210-2717
e-ISSN
—
Svazek periodika
6
Číslo periodika v rámci svazku
6
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
16
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—