Napjatostní a spolehlivostní analýza keramické hlavice totální kyc(elní endoprotézy s makro a mikro tvarovými odchylkami

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F08%3APU79937" target="_blank" >RIV/00216305:26210/08:PU79937 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61388998:_____/08:00322478

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Stress and Reliability Analyses of the Hip Joint Endoprosthesis Ceramic Head with Macro and Micro Shape Deviations

Popis výsledku v původním jazyce

The principal aim of this work is finding the reasons of the head's fractures because in the Czech Republic, some time ago, in vivo fracture of ceramic heads of total hip joint endoprostheses has been stated in a not negligible number of patients. The reliability of the ceramic head is based on the Weibull weakest link theory. The probability of the failure depends on the tensile stress values in the head, on the volume in which stress acts and on the material parameters of the used bioceramics (aluminium oxide). The stress analyses of the ceramic heads were realized using computational modelling - FEM system ANSYS under ISO 7206-5 loading. The maximum values of the tensile stress (the first principal stress) in the ceramic head are significantly influenced on the shape deviations of conical surfaces of the head and the stem cones. There are two types of the shape deviations - the first is macro deviations (different angle of the taper of the stem cone and the head cone), the second is

Název v anglickém jazyce

Stress and Reliability Analyses of the Hip Joint Endoprosthesis Ceramic Head with Macro and Micro Shape Deviations

Popis výsledku anglicky

The principal aim of this work is finding the reasons of the head's fractures because in the Czech Republic, some time ago, in vivo fracture of ceramic heads of total hip joint endoprostheses has been stated in a not negligible number of patients. The reliability of the ceramic head is based on the Weibull weakest link theory. The probability of the failure depends on the tensile stress values in the head, on the volume in which stress acts and on the material parameters of the used bioceramics (aluminium oxide). The stress analyses of the ceramic heads were realized using computational modelling - FEM system ANSYS under ISO 7206-5 loading. The maximum values of the tensile stress (the first principal stress) in the ceramic head are significantly influenced on the shape deviations of conical surfaces of the head and the stem cones. There are two types of the shape deviations - the first is macro deviations (different angle of the taper of the stem cone and the head cone), the second is

Druh

D - Stať ve sborníku

CEP obor

BO - Biofyzika

OECD FORD obor

—

Projekt

<a href="/cs/project/1P05ME789" target="_blank" >1P05ME789: Simulace mechanické funkce vybraných prvků lidského těla</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

13th International Conference on Biomedical Engineering

ISBN

978-3-540-92840-9

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

—

Název nakladatele

Springer

Místo vydání

Singapore

Místo konání akce

Singapore

Datum konání akce

3. 12. 2008

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—