Quantitative fractography of fish-eye crack formation under bending-torsion fatigue

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F10%3APU85475" target="_blank" >RIV/00216305:26210/10:PU85475 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Quantitative fractography of fish-eye crack formation under bending-torsion fatigue

Popis výsledku v původním jazyce

The paper presents results of the fractographical analysis of fish-eye cracks that were formed in plasmanitrided steel specimens under symmetrical bending, symmetrical torsion and biaxial in-phase bending-torsion loading combinations. Due to higher strength and compressive residual stresses introduced by plasma nitriding procedure, the subsurface fish-eye cracks were initiated inside the specimen bulk as a dominant failure mechanism. The geometrical characteristics of the fish-eye cracks (the radial asymmetry, the average size and the elliptical coefficient) were studied in the relation to the fish-eye crack location, the loading regime and the fatigue life. Both the ompressive residual stresses and the bending-torsion loading gradients were taken intoaccount when discussing the results. Besides the well known fact that the nitrided surface layer reduces the crack growth rate, the study revealed that the average size of the fish-eye crack increases with both the distance from the free

Název v anglickém jazyce

Quantitative fractography of fish-eye crack formation under bending-torsion fatigue

Popis výsledku anglicky

The paper presents results of the fractographical analysis of fish-eye cracks that were formed in plasmanitrided steel specimens under symmetrical bending, symmetrical torsion and biaxial in-phase bending-torsion loading combinations. Due to higher strength and compressive residual stresses introduced by plasma nitriding procedure, the subsurface fish-eye cracks were initiated inside the specimen bulk as a dominant failure mechanism. The geometrical characteristics of the fish-eye cracks (the radial asymmetry, the average size and the elliptical coefficient) were studied in the relation to the fish-eye crack location, the loading regime and the fatigue life. Both the ompressive residual stresses and the bending-torsion loading gradients were taken intoaccount when discussing the results. Besides the well known fact that the nitrided surface layer reduces the crack growth rate, the study revealed that the average size of the fish-eye crack increases with both the distance from the free

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GP106%2F08%2FP366" target="_blank" >GP106/08/P366: 3D analýza morfologie povrchů generovaných únavovým zatěžováním</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

INTERNATIONAL JOURNAL OF FATIGUE

ISSN

0142-1123

e-ISSN

—

Svazek periodika

32

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

8

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—